Behavior of ZrO_2-C Refractories in Thin-strip Casting of Steel
Behavior of ZrO_2-C Refractories in Thin-strip Casting of Steel
摘要
Zirconia graphite refractory is used as a core-nozzle in the thin-strip casting of steel. Post-mortem analysis of used refractory was performed in an effort to establish the failure mechanism. Corrosion behavior was studied against molten steel with Mn O- SiO 2based liquid inclusions. Corrosion of these materials involves dissolution and oxidation of graphite in the matrix followed by penetration of liquid slag leading to degradation of ZrO 2particles. Thermodynamic equilibrium calculations were performed to study this corrosion mechanism.
Zirconia graphite refractory is used as a core-nozzle in the thin-strip casting of steel. Post-mortem analysis of used refractory was performed in an effort to establish the failure mechanism. Corrosion behavior was studied against molten steel with Mn O- SiO 2based liquid inclusions. Corrosion of these materials involves dissolution and oxidation of graphite in the matrix followed by penetration of liquid slag leading to degradation of ZrO 2particles. Thermodynamic equilibrium calculations were performed to study this corrosion mechanism.
参考文献16
-
1B R Marple, S Poudrette, and F G Hamel. Ceramies for strip casting steel: Corrosion by liquid metal. 75 Steel- making Conference Proceedings, Toronto, Canada, 1992.
-
2G McQuillis. Method of thin strip casting. USA patent, US20140262121 A1, Sept. 18, 2014.
-
3R Mahapatra, W Blejde, G Gillen, P Campbell, and R Wechsler. The status of twin-roll strip casting technology - CASTRIP process. SCANMET II - 2nd International Conference on Process Development in Iron and Steel- making, Lulea, Swedeu, 2004.
-
4CASTRIP LLC: www. castrip, com.
-
5W. E. Lee, and S. Zhang. Melt corrosion of oxide and oxide- carbon refraetories. Inlernational Malerials Re- views, 1999, 44 (3) : 77 -104.
-
6Abhishek Kumar, Vivek Thapliyal and Jeffrey Smith. Interaction of BN - ZrO2 - SiC ceramics with inclusions in Si-killed steel, lnternalional Journal of Applied Ce- ramic Technology, 2014, 11 (6) : 1001 - 1014.
-
7V. Thapliyal, A. Kumar, D. G. C. Robertson, J. D. Smith. Transient inelusion formation and evolution in silicon killed steels, lronmaking & Steelmaking, 2015 (accepted). DOI: http://dx, doi. org/10. 1179/ 1743281214Y. 0000000241.
-
8A Kumar, V Thapliyal, D G C Robertson, and J D Smith. Kinetics of corrosion of BN - ZrO, - SiC ceram- ics in contact wiltl Si-killed steel. Journal of the Ameri- can Ceramic Society, 2015 (accepted). DOI: 10. 1111/jace. 13429.
-
9A. F. Dick, X. Yu, R. J. Pomfret, K. S. Coley. At- tack of submerged entry nozzles by mouht flux and disso- lution of refractory oxides in the flux. ISIJ International, 1997, 37(2) : 102 - 108.
-
10K Oki, M Sugie, K Kurihara, and Y Aiba. Wear pat- tern of zireonia refraetories by molten steel and slag. In Preprint of 1st Int. Conf. on Refractories, 1983,Tokyo, Japan, 721 -735.
-
1李庭寿.连铸用含石墨耐火材料[J].耐火材料,1989,23(3):51-54.
-
2HUANG Jiayuan,YANG Min,WANG Ziqiang,WANG Dongdong,ZHOU Huijun,YU Lingyan,JIANG Xin.Key Refractories Application in Hazelett Strip-casting Process[J].China's Refractories,2016,25(4):29-32.
-
3Brezng,B,陆美亚.镁—石墨耐火材料中方镁石与炭的反应性[J].国外耐火材料,1990,15(6):61-66.
-
4恒次邦男,崔学正.含石墨耐火材料中B4C的定量分析[J].国外耐火材料,1992,17(4):66-70.
-
5Luba.,NC,徐庆斌.碳结合剂对镁石墨耐火材料气孔率形成的影响[J].国外耐火材料,1989,14(6):20-25.
-
6利田正一,刘阿一.原料粒度和氧化物含量对含石墨耐火材料断裂性能的影响[J].国外耐火材料,1992,17(6):54-58.
-
7Beu,DA,黎非.氧化镁—石墨耐火材料的热震性[J].国外耐火材料,1992,17(5):59-61.
-
8恒次邦男,张利华.含石墨耐火材料B4C的宣分析[J].国外耐火材料,1991,16(7):27-28.
-
9Bahe.,BH,刘翠琴.氧化镁—石墨耐火材料中致密层的形成[J].国外耐火材料,1992,17(10):37-42.
-
10周红,王勇.Microstructure and corrosion mechanism of as-cast Mg-Zn-Mn-Ca in Hank's solution[J].Journal of Chongqing University,2010,9(3):146-150. 被引量：1