A new 3D copper(I) iodide hybrid, [Cu4I4(TMEDA)2]n (1, TMEDA = N,N,N',N'- tetramethylethylenediarnine), has been solvothermally synthesized and characterized by single- crystal X-ray diffraction, IR spectroscopy, elemental analysis, powder X-ray diffractions and thermogravimetric analysis. Compound 1 crystallizes in tetragonal space group P42/n with a = b = 11.5663(7) A, c = 9.2456(11) A, V= 1236.87(18) A3, Z = 8, C3H8CuIN, Mr = 248.54, Dc = 3.507 g/cm3, F(000) = 920, μ(MoKa) = 8.388 mm-1, the final R = 0.0244 and wR = 0.0573 for 1118 observed reflections (I 〉 20(/)). The hybrid framework is built up from cubane-like Cu4I4 cluster and flexible acyclic aliphatic diamine TMEDA, which can be simplified into a twofold interpenetrating dia network. The solid state luminescence spectrum displays a strong yellow emission band at room temperature (λex = 340 nm, λem = 530 nm). Results reveal that steric effect of N-substituted methyl groups in TMEDA have obvious influence on the structure and photoluminescent property of compound 1.
A new 3D copper(I) iodide hybrid, [Cu4I4(TMEDA)2]n (1, TMEDA = N,N,N',N'- tetramethylethylenediarnine), has been solvothermally synthesized and characterized by single- crystal X-ray diffraction, IR spectroscopy, elemental analysis, powder X-ray diffractions and thermogravimetric analysis. Compound 1 crystallizes in tetragonal space group P42/n with a = b = 11.5663(7) A, c = 9.2456(11) A, V= 1236.87(18) A3, Z = 8, C3H8CuIN, Mr = 248.54, Dc = 3.507 g/cm3, F(000) = 920, μ(MoKa) = 8.388 mm-1, the final R = 0.0244 and wR = 0.0573 for 1118 observed reflections (I 〉 20(/)). The hybrid framework is built up from cubane-like Cu4I4 cluster and flexible acyclic aliphatic diamine TMEDA, which can be simplified into a twofold interpenetrating dia network. The solid state luminescence spectrum displays a strong yellow emission band at room temperature (λex = 340 nm, λem = 530 nm). Results reveal that steric effect of N-substituted methyl groups in TMEDA have obvious influence on the structure and photoluminescent property of compound 1.
基金
supported by the Natural Scientific Foundation Committee of China(No.21171110)
the High and New Technology Industrialization Project in Colleges and Universities of Shanxi Province(No.20110016)