摘要
The Cr：Fe ratio （chromium-to-iron mass ratio） of chromite affects the production of chrome-based ferroalloys. Although the lit- erature contains numerous reports related to the magnetic separation of different minerals, limited work concerning the application of mag- netic separation to fine chromite from the Sukinda region of India to enhance its Cr：Fe ratio has been reported. In the present investigation, magnetic separation and mineralogical characterization studies of chromite fines were conducted to enhance the Cr：Fe ratio. Characterization studies included particle size and chemical analyses, X-ray diffraction analysis, automated mineral analysis, sink-and-float studies, and mag- netic susceptibility measurements, whereas magnetic separation was investigated using a rare earth drum magnetic separator, a rare earth roll magnetic separator, an induced roll magnetic separator, and a wet high-intensity magnetic separator. The fine chromite was observed to be upgraded to a Cr：Fe ratio of 2.2 with a yield of 55.7% through the use of an induced roll magnetic separator and a feed material with a Cr：Fe ratio of 1.6.
The Cr：Fe ratio （chromium-to-iron mass ratio） of chromite affects the production of chrome-based ferroalloys. Although the lit- erature contains numerous reports related to the magnetic separation of different minerals, limited work concerning the application of mag- netic separation to fine chromite from the Sukinda region of India to enhance its Cr：Fe ratio has been reported. In the present investigation, magnetic separation and mineralogical characterization studies of chromite fines were conducted to enhance the Cr：Fe ratio. Characterization studies included particle size and chemical analyses, X-ray diffraction analysis, automated mineral analysis, sink-and-float studies, and mag- netic susceptibility measurements, whereas magnetic separation was investigated using a rare earth drum magnetic separator, a rare earth roll magnetic separator, an induced roll magnetic separator, and a wet high-intensity magnetic separator. The fine chromite was observed to be upgraded to a Cr：Fe ratio of 2.2 with a yield of 55.7% through the use of an induced roll magnetic separator and a feed material with a Cr：Fe ratio of 1.6.