摘要
以3-(4-氯苯基)戊二酸(H2CPGA)为主要配体采用微波合成法合成了一个锌的新型配位聚合物[Zn(HCPGA)2(H2O)2]n(1),用元素分析仪、荧光光谱仪、红外光谱仪、热重分析仪和单晶衍射仪等对其进行了表征。结果表明该配位聚合物属于单斜晶系,空间群是C2/c。晶胞参数:a=2.9922(12)nm,b=0.7370(3)nm,c=1.0924(4)nm,β=98.008(6)°,F(000)=1200,Dc=1.628 g·cm-3,V=2.3855(16)nm3,Mr=584.68,Z=4,μ=1.309 mm-1,R1=0.0352,wR2=0.1124。
A new Zn( Ⅱ) coordination polymer [Zn( HCPGA)2( H2O)2]n( 1),was produced with 3-( 4-Chlorophenyl) glutaric acid by microwave synthesis. The coordination polymer was characterized by elemental analysis,IR spectroscopy,fluorescence spectrometer,thermal analysis,and X-ray singlecrystal diffraction and so on. The results indicate that coordination complex crystallizes in the monoclinic system,space group C2 / c. The cell parameters: a = 2. 9922( 12) nm,b = 0. 7370( 3) nm,c = 1. 0924( 4) nm,β = 98. 008( 6) °,F( 000) = 1200,Dc= 1. 628 g·cm- 3,V = 2. 3855( 16) nm3,Mr= 584.68,Z = 4,μ = 1. 309 mm- 1,R1= 0. 0352,wR2= 0. 1124.
出处
《人工晶体学报》
EI
CAS
CSCD
北大核心
2015年第3期841-845,共5页
Journal of Synthetic Crystals
基金
安徽省教育厅自然基金(KJ2012A268
KJ2013B292)
宿州学院平台课题(2014YKF36
2013YKF20)
宿州学院创新团队建设计划(2013KYTD02)
安徽省自然科学基金(1408085QB41)
安徽省教育厅自然科学研究项目(KJ2013A247)
宿州学院创新项目(201410379072)