摘要
A systemic investigation was done on the chemistry and crystal structure of boundary phases in sintered Ce9Nd21FebalB1 （wt%） magnets. Ce2Fe14B is believed to be more soluble in the rare-earth （RE）-rich liquid phase during the sintering process. Thus, the grain size and oxygen content were controlled via low-temperature sintering, resulting in high coercivity and maximum energy products. In addition, Ce formed massive agglomerations at the triple-point junctions, as confirmed by elemental mapping results. Transmission electron micros- copy （TEM） images indicated the presence of （Ce,Nd）Ox phases at grain boundaries. By controlling the composition and optimizing the preparation process, we successfully obtained Ce9Nd21FebalBx sintered magnets; the prepared magnets exhibited a residual induction, coerciv- ity, and energy product of 1.353 T, 759 kA/m, and 342 kJ/m3, respectively.
A systemic investigation was done on the chemistry and crystal structure of boundary phases in sintered Ce9Nd21FebalB1 （wt%） magnets. Ce2Fe14B is believed to be more soluble in the rare-earth （RE）-rich liquid phase during the sintering process. Thus, the grain size and oxygen content were controlled via low-temperature sintering, resulting in high coercivity and maximum energy products. In addition, Ce formed massive agglomerations at the triple-point junctions, as confirmed by elemental mapping results. Transmission electron micros- copy （TEM） images indicated the presence of （Ce,Nd）Ox phases at grain boundaries. By controlling the composition and optimizing the preparation process, we successfully obtained Ce9Nd21FebalBx sintered magnets; the prepared magnets exhibited a residual induction, coerciv- ity, and energy product of 1.353 T, 759 kA/m, and 342 kJ/m3, respectively.
基金
financially supported by the National Natural Science Foundation of China (No. 51171048)
the National High Technology Research and Development Program of China (No. 2014CB643701)
the National Science and Technology Support Program of China (No. 2012BAE02B01)