The effect of the volume fraction of ferromagnetic metal （x） in （Ni75Fe25）x（ZnO）1-x nanogranular thin films on microstructural, soft-magnetic, and high-frequency properties was investigated. Good soft-magnetic properties were obtained in a broad x range, with 0.55 〈 x 〈 0.82. High resolution transmission electron microscopy （HRTEM） observations reveal that the grain size of the samples is lower than 14 nm, and that it decreases with decreasing x. Of special interest, our investigation of the permeability spectra indicates that these films exhibit an adjustable frequency linewidth of resonance peak, dependant upon changing x. Correspondingly, large and adjustable damping coefficients （aeff） from 0.023 to 0.043 were achieved by decreasing x from 0.82 to 0.55. Combined with the HRTEM results, the variation of αeff with x was analyzed in detail.
The effect of the volume fraction of ferromagnetic metal （x） in （Ni75Fe25）x（ZnO）1-x nanogranular thin films on microstructural, soft-magnetic, and high-frequency properties was investigated. Good soft-magnetic properties were obtained in a broad x range, with 0.55 〈 x 〈 0.82. High resolution transmission electron microscopy （HRTEM） observations reveal that the grain size of the samples is lower than 14 nm, and that it decreases with decreasing x. Of special interest, our investigation of the permeability spectra indicates that these films exhibit an adjustable frequency linewidth of resonance peak, dependant upon changing x. Correspondingly, large and adjustable damping coefficients （aeff） from 0.023 to 0.043 were achieved by decreasing x from 0.82 to 0.55. Combined with the HRTEM results, the variation of αeff with x was analyzed in detail.
基金
Project supported by the National Natural Science Foundation of China(Grant Nos.50901050 and 51101079)