摘要
采用热浸镀工艺模拟试验机进行了镀锌工艺研究,研究试验钢在不同的浸润时间和露点的条件下,镀层重量和厚度的分布情况。结果显示,在露点不变的情况下,镀层重量和厚度随浸润时间的延长而增加,但是厚度的变化范围相对较小;当浸润时间不变时,随着露点从-10℃降低到-60℃,镀层重量和厚度变化趋势相同,均在-30℃时获得最大值。
The distribution of coating weight and coating thickness under the di^ferent dipping times and dew points were studied by a hot dipping process simulator. The results showed that when dew point stabilized, the coating weight and thickness of experimental steel increased with the increased immersion times, but the variation of thickness was relatively small, and that when immersion times stabilized and dew point dropped from -- 10℃ to -- 60℃, the alteration trend of weight and thickness was the same, reaching the maximum value in dew point of --30℃.
出处
《武汉工程职业技术学院学报》
2015年第1期25-27,共3页
Journal of Wuhan Engineering Institute
关键词
浸润时间
露点
镀层重量
镀层厚度
dipping time
dew point
coating weight
coating thickness