A series of color-tunable KLaSiO4：Ce3＋,Mn2＋phosphors were successfully prepared and the luminescent properties were investigated. Upon excitation at 290 nm, the emission spectra of KLaSiO4：Ce3＋,Mn2＋phosphors included a blue emission band and a red emission band. Increasing the doping concentration of Mn2＋ions, the red emission was strengthened considerably, and the blue emission of Ce3＋ was reduced, owing to the efficient energy transfer. The composition optimized KLa0.96SiO4：0.02Ce3＋,0.02Mn2＋sample exhibited the white light emission brightly with the chromaticity coordinates of （0.331, 0.337）. Therefore, KLaSiO4：Ce3＋, Mn2＋could be used as a white phosphor candidate for white light-emitting diodes devices.
A series of color-tunable KLaSiO4：Ce3＋,Mn2＋phosphors were successfully prepared and the luminescent properties were investigated. Upon excitation at 290 nm, the emission spectra of KLaSiO4：Ce3＋,Mn2＋phosphors included a blue emission band and a red emission band. Increasing the doping concentration of Mn2＋ions, the red emission was strengthened considerably, and the blue emission of Ce3＋ was reduced, owing to the efficient energy transfer. The composition optimized KLa0.96SiO4：0.02Ce3＋,0.02Mn2＋sample exhibited the white light emission brightly with the chromaticity coordinates of （0.331, 0.337）. Therefore, KLaSiO4：Ce3＋, Mn2＋could be used as a white phosphor candidate for white light-emitting diodes devices.
基金
Project supported by the Gansu Industry and Information Technology Committee(773000054000001)
the Fundamental Research Funds for the Central Universities(lzujbky-2014-37)
Specialized Reserch Fund for the Doctoral Program of Higher Education(20120211130003)
the National Natural Science Foundation of China(51372105)