By using a static and high-speed material testing machine, tensile deformation behaviors of two kinds of Si- Mn TRIP （transformation induced plasticity） steels and DP （dual phase） steel were studied in a large range of strain rates （0.001-2000 s 1）. Temperature variation during adiabatic heating and the amount of retained austenite at fracture were measured by an infrared thermometer and an Xray stress analyser, respectively. The microstructure of steels was observed by optical microscopy （OM） and scanning electron microscopy （SEM） before and after tensile test. It was found from the experimental results that the tensile strength of these steels increased, and the fracture elonga- tion firstly decreased and subsequently increased, as the strain rate increased in the range ＂of 0.1 - 2000 s -1. The temperature raised during adiabatic heating of TRIP steel was in the range of 100- 300℃, while that of the DP steel was in the range of 100-220℃ . The temperature rise of these steels increased with increasing the strain rate, as well as the amount of the transformed retained austenite in TRIP steels. It was confirmed that austenite to martensite transformation is not suppressed by adiabatic heating.
By using a static and high-speed material testing machine, tensile deformation behaviors of two kinds of Si- Mn TRIP （transformation induced plasticity） steels and DP （dual phase） steel were studied in a large range of strain rates （0.001-2000 s 1）. Temperature variation during adiabatic heating and the amount of retained austenite at fracture were measured by an infrared thermometer and an Xray stress analyser, respectively. The microstructure of steels was observed by optical microscopy （OM） and scanning electron microscopy （SEM） before and after tensile test. It was found from the experimental results that the tensile strength of these steels increased, and the fracture elonga- tion firstly decreased and subsequently increased, as the strain rate increased in the range ＂of 0.1 - 2000 s -1. The temperature raised during adiabatic heating of TRIP steel was in the range of 100- 300℃, while that of the DP steel was in the range of 100-220℃ . The temperature rise of these steels increased with increasing the strain rate, as well as the amount of the transformed retained austenite in TRIP steels. It was confirmed that austenite to martensite transformation is not suppressed by adiabatic heating.
基金
Sponsored by National Natural Science Foundation of China(50934011,50971137)
National Basic Research Program of China(2010CB630802)