A modified nonlinear fatigue damage accumulation model based on the Manson-Halford theory was presented,and the new model was developed for fatigue life prediction under constant and variable amplitude loading, which took the effects of the load interactions and the phenomenon of material's strength degradation into account. The experimental data of the 30 Cr Mn Si A and the LY-12 cz from literature were used to verify the proposed model. And from the good agreement between the experimental data and predicted results,we can see it clear that the proposed method can be applied to predicting fatigue life under different loadings.
A modified nonlinear fatigue damage accumulation model based on the Manson-Halford theory was presented,and the new model was developed for fatigue life prediction under constant and variable amplitude loading, which took the effects of the load interactions and the phenomenon of material＇s strength degradation into account. The experimental data of the 30 Cr Mn Si A and the LY-12 cz from literature were used to verify the proposed model. And from the good agreement between the experimental data and predicted results,we can see it clear that the proposed method can be applied to predicting fatigue life under different loadings.
基金
National Natural Science Foundation of China(No.11272082)
Fundamental Research Funds for the Central Universities(No.E022050205)
the Open Research Fund of Key Laboratory of Fluid and Power Machinery of Xi Hua University,China(No.szjj2013-03)