增氮对钒微合金钢组织和性能的影响 被引量:15

Influence of nitrogen addition on the microstructure and properties of vanadium microalloyed steel
原文传递
导出
摘要 通过对不同钒、氮质量分数的试验钢进行热模拟压缩试验和实验室轧制试验,用OM、SEM和TEM分析试验钢的显微组织,研究增氮对钒微合金钢组织和性能的影响。结果表明,普通钒微合金钢为板条贝氏体+粒状贝氏体组织,增加氮质量分数,可促进晶内铁素体相变,得到针状铁素体组织,使M/A组织细化且弥散分布,改善韧性;而增加钒质量分数,可以增加析出强化作用,提高强度,但组织形态无明显变化,不能提高韧性。增氮钢中的钒在奥氏体内以VN析出,低氮钢内的钒在铁素体内以VC的形式析出,奥氏体-铁素体、VC-铁素体和VN-铁素体的平面点阵错配度分别为6.72%、3.89%和1.55%,在奥氏体内析出的VN可以作为铁素体的优先形核位置,促进晶内铁素体相变。 The influence of nitrogen addition on the microstructure and mechanical properties of vanadium microalloyed steel was studied. Experiment steels with different vanadium and nitrogen content were processed by thermal deforming simulation and rolled by laboratory roller respectively. OM, SEM and TEM were used to investigate the microstructure. Test results show that bainite laths and granular bainite are dominant in base vanadium microalloying steel. Intragranular ferrite trasnformation is promoted by nitrogen addition, which leads to acicular ferrite microstructure and refines the martensite-austeniete component. The toughness is improved as well. However, addition of vanadium increases precipitation strengthening, but has little effect on the morphology. The toughness is not improved. Vanadium precipitates in austenite as VN for nitrogen-rich steel. While for the nitrogen-low steels, it precipitates in ferrite as VC even if the content of vanadium is increased. The lattice misfit degree of austenite-ferrite, VC-ferrite and VN-ferrite are 6.72%, 3.89% and 1.55% respectively. It indicates that VN precipitated in austenite acts as preferential nucleation sites and promotes the intragranular ferrite transformation.
出处 《钢铁》 CAS CSCD 北大核心 2015年第4期63-69,共7页 Iron and Steel
基金 工信部高技术船舶科研项目资助项目
关键词 钒微合金化 增氮 晶内铁素体相变 韧性 平面点阵错配度 vanadium microalloyed steel nitrogen addition intragranular ferrite transformation toughness planar lattice misfit degree
  • 相关文献

参考文献17

  • 1Kern A, Nisessen T, Schriever U, et al. Production and proper- ties of thermomechanically rolled high strength steel plates with minimum yield strengths up to 700 MPa[J]. Ironmaking and Steelmaking, 2005, 32 (4): 331.
  • 2杨才福,张永权.钒氮微合金化技术在HSLA钢中的应用[J].钢铁,2002,37(11):42-47. 被引量:85
  • 3Ishikawa F, Takahashi T, Ochi T. Intragranular ferrite nucleation in medium-carbon vanadium steels[J]. Metall Mater Trans: A, 1994,25(5): 929.
  • 4龚维幂,杨才福,张永权.钒氮钢中的晶粒细化研究[J].钢铁研究学报,2006,18(10):49-53. 被引量:26
  • 5Tsunekage N, Kobayashi K, Tsubakino H. Influence of sulphur and vanadium additions on toughness of bainitic steels[J]. Mate- rials Science and Technology, 2001,17 (7): 847.
  • 6Lagneborg R, Siwecki T, Zajac S, et al. The role of vanadium in microallyed steels[M]. Stockholm: The Scandanavian Journal of Metallurgy, 1999.
  • 7Senuma T. Present status of and future prospects for precipita- tion research in the steel industry[J]. ISIJ International, 2002, 42 (1):1.
  • 8Ishikawa F, Takahashi T. The formation of intragranular ferrite plates in medium-carbon steels for hot-forging and its effect on the toughness[J]. ISIJ International, 1995,35(9): 1128.
  • 9Siwecki T. Vanadium microalloyed bainitic hot strip steels[J]. ISIJ International, 2010, 50 (5): 760.
  • 10Nakai K, Sakamoto T, Asakura R, et al. Nucleation of bainite at small angle dislocation network in austenite and its effects on mechanical properties in steels[J]. ISIJ International, 2011, 51 (2):274.

二级参考文献35

共引文献168

同被引文献150

引证文献15

二级引证文献48

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部