To explore the temperature dependence of deformation behavior of BCC structural materials and the relevant effect of pre-annealing, commercially pure iron （CP Fe） produced by equal-channel angular pressing （ECAP） is selected as the experimental material. The influences of deformation temperature T and pre-annealing on deformation behavior, surface deformation characteristics and substructures of ECAP Fe were systematically studied. The results show that ECAP Fe undergoes a remarkable strain softening stage after a rapid strain hardening during uniaxial compression, and the softening degree and the yield strength avs first decrease and then increase with raising temperature. Pre-annealing at 400 ℃ effectively weakens the strain softening degree and increases trys. To understand the influence of deformation temperature on deformation behavior, as well as the relevant pre-annealing effect, deformation and damage characteristics and dislocation structures are studied in detail. In a word, the strain softening of ECAP Fe is associated not only with internal structural instability, but also with temperature, and pre-annealing at 400 ℃ improves high-temperature me- chanical properties of ECAP Fe.
To explore the temperature dependence of deformation behavior of BCC structural materials and the relevant effect of pre-annealing, commercially pure iron （CP Fe） produced by equal-channel angular pressing （ECAP） is selected as the experimental material. The influences of deformation temperature T and pre-annealing on deformation behavior, surface deformation characteristics and substructures of ECAP Fe were systematically studied. The results show that ECAP Fe undergoes a remarkable strain softening stage after a rapid strain hardening during uniaxial compression, and the softening degree and the yield strength avs first decrease and then increase with raising temperature. Pre-annealing at 400 ℃ effectively weakens the strain softening degree and increases trys. To understand the influence of deformation temperature on deformation behavior, as well as the relevant pre-annealing effect, deformation and damage characteristics and dislocation structures are studied in detail. In a word, the strain softening of ECAP Fe is associated not only with internal structural instability, but also with temperature, and pre-annealing at 400 ℃ improves high-temperature me- chanical properties of ECAP Fe.
基金
financially supported by the National Natural Science Foundation of China (Nos. 51231002, 51271054, 51201077 and 50671023)
the Specialized Research Fund for the Doctoral Program of Higher Education of China (No. 20110042110017)
the Fundamental Research Funds for the Central Universities of China (Nos. N110105001 and N120505001)