反应性阻燃剂N-(2,4,6-三溴苯基)马来酰亚胺改性聚甲基丙烯酰亚胺(PMI)泡沫的制备与性能研究 被引量:7

Preparation and Characterization of Modified Polymethacrylimide(PMI)Foams Derived from Reactive Flame Retardant N-(2,4,6-tribromophenyl)Maleimide
下载PDF
导出
摘要 采用N-(2,4,6-三溴苯基)马来酰亚胺(TBPMI)作为反应性阻燃剂与甲基丙烯酸、丙烯腈共聚,通过调节反应性阻燃剂的用量成功制备了不同的改性聚甲基丙烯酰亚胺(PMI)泡沫。研究结果表明,经TBPMI改性的PMI泡沫的T_g均在212℃左右,经过200℃处理2h后,可进一步提高泡沫的T_g。改性后泡沫的热稳定性明显提高,10%热失重温度为485℃,高于未改性PMI泡沫28℃。改性泡沫的压缩强度为0.6~1.3 MPa。随TBPMI含量的增加,改性泡沫的阻燃性能明显提高,极限氧指数(LOI)值从26.0逐渐升高至28.0,火焰垂直燃烧熄灭时间按则从13.1s下降至3.8 s。 A series of modified polymethacrylimide (PMI) foams were successfully prepared via compolymerization of methacrylic acid, acrylonitrile and reactive flame retardants N-(2,4,6-tribromophenyl) maleimide (TBPMI) by added different weight ratio of TBPMI, respectively. And the modified PMI foams were widely researched. The results showed that Tgs of modified foams were all about 212 ℃ and Tss could be further elevated by treated at 200 ℃ for 2 hours. The thermostability of foams was obviously improved as thermogravimetic analysis shows that 10% weight loss temperatures of TBPMI modified foams were around 485.8℃ ,about 28℃higher than the corresponding neat PMI foam. The compressive strength of TBPMI modified foams ranged from 0.6 to 1.3 MPa which were close to neat PMI foam. The limited oxygen index (LOI) were elevated from 26.0 to 28.0, meanwhile the extinguish times in the vertical flame burning test were reduced from 13.1 s to 3.8 s with the content of TBPMI increasing in the modified PMI foams.
出处 《上海塑料》 2015年第1期21-26,共6页 Shanghai Plastics
基金 国家商用飞机制造工程技术研究中心创新基金(SAMC-12-JS-15-011)
关键词 聚甲基丙烯酰亚胺 阻燃性 反应性阻燃剂 N-(2 4 6-三溴苯基)马来酰亚胺 polymethacrylimide flammability reactive flame retardants N-(2,4,6-tribromophenyl) maleimide
  • 相关文献

参考文献20

二级参考文献29

共引文献109

同被引文献40

引证文献7

二级引证文献26

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部