Effects of direct ultrasonic treatment on microstructure and elongation of semi-solid Sn-62Bi alloy

Effects of direct ultrasonic treatment on microstructure and elongation of semi-solid Sn-62Bi alloy
下载PDF
导出
摘要 A new direct ultrasonic treatment(DUT) setup with the ultrasonic horn placed in the horizontal direction was developed and used in the preparation of semi-solid Sn-62 Bi slurry. The influence of DUT temperature on microstructure and properties of Sn-62 Bi alloy were studied. The test results of XRD showed that the semi-solid Sn-62 Bi alloy obtained by the DUT process exhibits pronounced preferential orientation of Bi(2 0 2), Bi(-1 1 1), Bi(-2 0 1), Sn(1 1 0) and Sn(2 2 0) planes. Compared to the conventional liquid casting Sn-62 Bi alloy without DUT, it was discovered that the primary Bi blocks of semi-solid Sn-62 Bi alloy prepared with the DUT process distribute more homogeneously and are smaller. With the treatment by ultrasonic vibration in the semi-solid state for 120 s, the higher the primary Bi phase fraction in the slurry, the smaller the size of primary semi-solid Bi blocks formed after solidification. The average side length of the primary Bi blocks was from 30 μm to 80 μm. The elongation of Sn-62 Bi alloy treated by DUT for 120 s at 145 °C is 43.21%, reflecting a distinctly improvement by 129.10%, as compared to the conventional liquid casting Sn-62 Bi alloy without DUT. This indicates that DUT process could improve dramatically the ductility of Sn-62 Bi alloys content. The microstructure evolution mechanism of semi-solid Sn-62 Bi alloy slurry was also analyzed. A new direct ultrasonic treatment(DUT) setup with the ultrasonic horn placed in the horizontal direction was developed and used in the preparation of semi-solid Sn-62 Bi slurry. The influence of DUT temperature on microstructure and properties of Sn-62 Bi alloy were studied. The test results of XRD showed that the semi-solid Sn-62 Bi alloy obtained by the DUT process exhibits pronounced preferential orientation of Bi(2 0 2), Bi(-1 1 1), Bi(-2 0 1), Sn(1 1 0) and Sn(2 2 0) planes. Compared to the conventional liquid casting Sn-62 Bi alloy without DUT, it was discovered that the primary Bi blocks of semi-solid Sn-62 Bi alloy prepared with the DUT process distribute more homogeneously and are smaller. With the treatment by ultrasonic vibration in the semi-solid state for 120 s, the higher the primary Bi phase fraction in the slurry, the smaller the size of primary semi-solid Bi blocks formed after solidification. The average side length of the primary Bi blocks was from 30 μm to 80 μm. The elongation of Sn-62 Bi alloy treated by DUT for 120 s at 145 °C is 43.21%, reflecting a distinctly improvement by 129.10%, as compared to the conventional liquid casting Sn-62 Bi alloy without DUT. This indicates that DUT process could improve dramatically the ductility of Sn-62 Bi alloys content. The microstructure evolution mechanism of semi-solid Sn-62 Bi alloy slurry was also analyzed.
出处 《China Foundry》 SCIE CAS 2015年第3期163-168,共6页 中国铸造(英文版)
基金 financially supported by the National Natural Science Foundation of China(Grant no.51104049)
关键词 direct ultrasonic treatment SEMI-SOLID SN-BI MICROSTRUCTURE ELONGATION direct ultrasonic treatment semi-solid Sn-Bi microstructure elongation
  • 相关文献

二级参考文献19

  • 1Rohatgi P K. ASM Handbook, vol 15: Casting, Materials Parks, Ohio, ASM International, 2008: 1149.
  • 2Gruzleski JE, Closset B M. The treatment of liquid aluminum silicon alloys, Schaumberg, IL: American Foundrymen's Society, 1990: 17.
  • 3Lu S Z, and Hellawell A. Growth Mechanisms of Silicon in AI-Si Alloys. J. Crystal Grow1h, 1985,73(2): 316--328.
  • 4Hanna M D, Lu S Z, and Hellawell A. Modification in the Aluminum Silicon System. Metall. Trans. A, 1984, 15(3): 459- 469.
  • 5Heiberg G, Nogita K, Dahle A K, and Arnberg L. Columnar to equiaxed transition of eutectic in hypoeutectic aluminium?silicon alloys. Acta Mater, 2002, 50: 2537-2546.
  • 6Jenkinson D C, and Hogan L M. The Modification of Aluminum?Silicon Alloys with Strontium. J. Cryst Growth, 1975, 28(2): 171-187.
  • 7Lu Z S, and Hellawell A. The Mechanism of Silicon Modification in Aluminum-Silicon Alloys: Impurity Induced Twinning. Metall Trans A, 1987, 18(10): 1721-1733.
  • 8Jie W, Chen Z, and Reif W. Superheat Treatment of AI-7Si- 0.55Mg Melt and Its Influences on the Solidification Structures and the Mechanical Properties. Metall Mater Trans A, 2003, 34(3): 799-806.
  • 9Atasoy 0 A, Yilmaz F, and Elliot R. Growth structures in aluminium-silicon alloys - I. The coupled zone. J. Cryst Growth, 1984,66(1): 137-146.
  • 10Han Q, and Jian X. Subject Invention # 1595, S-105, 197, Oak Ridge, Tennessee, USA, Oak Ridge National Laboratory, 2005.

共引文献11

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部