摘要
为了拓宽我国脱硫石膏的利用途径,实现对脱硫石膏直接利用,本研究选取谷氨酸钠作为缓凝剂,聚羧酸作为减水剂,对脱硫石膏现浇墙体材料进行改性研究。试验结果表明:电厂的脱硫石膏经过55℃预烘干2 h,160℃烘干3 h,按照GB/T 17669.4-1999确定标稠需水量,添加3%谷氨酸钠作为缓凝剂,0.5%聚羧酸作为减水剂时,现浇墙体材料的初凝时间约54 min,终凝时间延长至96 min,复配后初终凝时间满足施工要求;墙体材料的绝干抗折强度为3.31 MPa,绝干抗压强度为12.27 MPa。
In order to broaden the usage of desulfurization gypsum, and fulfill the directly use of it, Monosodium glutamate was selected as retarder, poly carboxylic acid was selected as reducing agent, effects of which on desulfurization gypsum cast-in-place wall material were studied. Desul-furization gypsum was prebaked for 2 hours at 55℃, and then burned for 3 hours at 160℃, the standard consistency water demand was determined according to GB/T 17669.4-1999. The experi-ment results were as follows:with adding 3%Monosodium glutamate as retarder, 0.5%Poly carbo-xylic acid as reducing agent, and initial setting time of desulfurization gypsum cast-in-place wall material is about 54 min and final setting time extends to 96 min, which meet the requirements of construction. Dry flexural strength of the wall material is 3.31 MPa, dry compressive strength is 12.27 MPa.
出处
《中国环境管理干部学院学报》
CAS
2015年第3期64-66,77,共4页
Journal of Environmental Management College of China
基金
唐山市科技支撑项目<脱硫石膏制备高性能墙体材料技术开发与示范>(12130204A-3)
关键词
脱硫石膏
缓凝剂
减水剂
初终凝时间
抗折抗压强度
desulfurization gypsum
retarder
water reducer
initial and final setting time
flexural and compressive strength