A sodium–zinc sorbent based flue gas desulfurization technology(Na–Zn-FGD) was proposed based on the experiments and analyses of the thermal decomposition characteristics of Ca SO3 and Zn SO3·2.5H2 O, the waste products of calcium-based semi-dry and zinc-based flue gas desulfurization(Ca–SD-FGD and Zn–SD-FGD) technologies, respectively. It was found that Zn SO3·2.5H2 O first lost crystal H2 O at 100 °C and then decomposed into SO2 and solid Zn O at 260 °C in the air, while Ca SO3 is oxidized at 450 °C before it decomposed in the air. The experimental results confirm that Zn–SD-FGD technology is good for SO2 removal and recycling, but with problem in clogging and high operational cost. The proposed Na–Zn-FGD is clogging proof, and more cost-effective. In the new process, Na2CO3 is used to generate Na2SO3 for SO2absorption, and the intermediate product Na HSO3 reacts with Zn O powders, producing Zn SO3·2.5H2 O precipitate and Na2SO3 solution. The Na2SO3 solution is clogging proof, which is re-used for SO2 absorption. By thermal decomposition of Zn SO3·2.5H2 O, Zn O is re-generated and SO2 with high purity is co-produced as well. The cycle consumes some amount of raw material Na2CO3 and a small amount of Zn O only. The newly proposed FGD technology could be a substitute of the traditional semi-dry FGD technologies.
A sodium–zinc sorbent based flue gas desulfurization technology（Na–Zn-FGD） was proposed based on the experiments and analyses of the thermal decomposition characteristics of Ca SO3 and Zn SO3·2.5H2 O, the waste products of calcium-based semi-dry and zinc-based flue gas desulfurization（Ca–SD-FGD and Zn–SD-FGD） technologies, respectively. It was found that Zn SO3·2.5H2 O first lost crystal H2 O at 100 °C and then decomposed into SO2 and solid Zn O at 260 °C in the air, while Ca SO3 is oxidized at 450 °C before it decomposed in the air. The experimental results confirm that Zn–SD-FGD technology is good for SO2 removal and recycling, but with problem in clogging and high operational cost. The proposed Na–Zn-FGD is clogging proof, and more cost-effective. In the new process, Na2CO3 is used to generate Na2SO3 for SO2absorption, and the intermediate product Na HSO3 reacts with Zn O powders, producing Zn SO3·2.5H2 O precipitate and Na2SO3 solution. The Na2SO3 solution is clogging proof, which is re-used for SO2 absorption. By thermal decomposition of Zn SO3·2.5H2 O, Zn O is re-generated and SO2 with high purity is co-produced as well. The cycle consumes some amount of raw material Na2CO3 and a small amount of Zn O only. The newly proposed FGD technology could be a substitute of the traditional semi-dry FGD technologies.
基金
Supported by the National High Technology Research and Development Program of China(2009AA05Z302)