摘要
The sensing performances of multiple networked Ga N nanowire(NW) sensor codecorated with Au and Pt nanoparticles were examined. The pristine Ga N nanowires show responses of approximately 108%-173% to 0.05%-0.25% H2 at room temperature. On the other hand, the Ga N nanowires decorated with Au and those decorated with Pt lead to 1.1-1.3 and 1.2-1.6 times,respectively, stronger responses to 0.05%-0.25% H2. In contrast, the Au Pt-codecorated Ga N nanowires show 1.3-2.0 times stronger responses to 0.05%-0.25% H2. In other words, the Ga N nanorods codecorated with Au and Pt nanoparticles show much stronger response to H2 gas than the Au or Pt monometal-decorated counterpart. The underlying mechanism for the enhanced response of the Au Pt-codecorated Ga N nanowire was discussed.
The sensing performances of multiple networked Ga N nanowire（NW） sensor codecorated with Au and Pt nanoparticles were examined. The pristine Ga N nanowires show responses of approximately 108%-173% to 0.05%-0.25% H2 at room temperature. On the other hand, the Ga N nanowires decorated with Au and those decorated with Pt lead to 1.1-1.3 and 1.2-1.6 times,respectively, stronger responses to 0.05%-0.25% H2. In contrast, the Au Pt-codecorated Ga N nanowires show 1.3-2.0 times stronger responses to 0.05%-0.25% H2. In other words, the Ga N nanorods codecorated with Au and Pt nanoparticles show much stronger response to H2 gas than the Au or Pt monometal-decorated counterpart. The underlying mechanism for the enhanced response of the Au Pt-codecorated Ga N nanowire was discussed.
基金
Project(2010-0020163)supported by Basic Science Research Program through the National Research Foundation(NRF)funded by the Ministry of Education of Korea