以丁二酸、丁二醇、1,6-己二胺为原料,二丁基二月桂酸锡为催化剂,甲苯二异氰酸酯(TDI)为扩链剂,通过熔融共聚,合成了M w为40-65k的聚丁二酸-丁二醇-1,6-己二胺共聚物,并采用压延成膜法制得聚酯酰胺薄膜.研究了1,6-己二胺含量对聚酯酰胺的热性能、结晶性能、降解性能和流变性能的影响.结果表明,合成了聚酯酰胺,其熔点达到100.97 ℃,热分解温度为317.85℃;随着1,6G己二胺添加量增加,聚酯酰胺的拉伸强度不断变大,断裂伸长率略有下降;1,6-己二胺的加入并未改变聚酯酰胺的晶型,但降低了其结晶度;1,6-己二胺的加入提高了聚酯酰胺降解性能,而且改善了其流变性能,这有利于聚酯酰胺的成型加工和应用.
Succinic acid-butanediol-1,6-hexamethylenediamine polyester amide copolymers with Mw from 40 000 to 65000 were synthesized by succinic acid,1,4-butylene and 1,6-hexamethylenediamine,through high temperature melt reaction. Meanwhile,the second dibutyl tin laurate was selected as catalyst,and the toluene disocyanate( TDI) was selected as chain extender. The succinic acid-butylene-adipic amine copolymer films were prepared by calendering film-forming method. The influences of the content of 1,6-adipic amine on the copolymer performance of thermal,crystallization,degradation and rheological properties were researched. The results showed that the polyester amide copolymers were synthesized successfully,whose melting point is 100. 97 ℃ and the thermal decomposition temperature is 317. 85 ℃. With the increasing of 1,6-adipic amine,the tensile strength of copolymers increased accordingly,and the elongation at break decreased slightly. 1,6-adipic amine did not change the crystal type of copolymer,but the crystallinity of copolymer decreased. With adding the 1,6-adipic amine in copolymer,the degradation performance and rheological properties of the copolymers were improved,which is useful for the further processing.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2015年第15期15099-15104,共6页
Journal of Functional Materials
基金
国家自然科学基金资助项目(11372108)
湖南省自然科学基金资助项目(14JJ5021)
湖南省高校创新平台开放基金资助项目(14K032
13K098)
关键词
生物可降解
聚酯酰胺
1
6G己二胺
丁二酸
丁二醇
熔融缩聚
degradable materials
polyester amide
1,6 hexamethylenediamine succinic acid
1,4 butanediol
melt polycondensation