Preparation of Sintered(Ce_(1-x)Nd_x)_(30)Fe_(bal)Cu_(0.1)B_1 Magnets by Blending Powder Method 被引量:1

Preparation of Sintered(Ce_(1-x)Nd_x)_(30)Fe_(bal)Cu_(0.1)B_1 Magnets by Blending Powder Method
原文传递
导出
摘要 Magnets with nominal compositions of ( Nd1-x Cex ) 30 Febal Cu0.1 B1 (x = 0, 0.15, 0.3 and 0.4, mass% ) have been fabricated by blending powder method. The remanence (B r), intrinsic coercivity (He) and maximum en- ergy product (BH) of the RE2Fe14B type magnets deteriorated when Nd was replaced by Ce. The chemical composition and crystal structure of magnet were investigated systemically. Backscattered electron (BSE) and energy dispersive spectroscopy (EDS) results revealed that Ce-rich and Ce-lean matrix grains coexisted in the magnets. The magnetic coupling mechanism among the double hard magnetic phases was discussed. Low melting point RE-Cu phase was in favor of the formation of uniform continuous grain boundary. Transmission electron microscopy (TEM) investigation showed the presence of fcc (Nd,Ce)Ox phase in the grain boundary. When the Ce content was 15% of the total amounts of all the rare earth, the maximum energy product of the sintered magnet was 359.8 kJ/ms. Magnets with nominal compositions of ( Nd1-x Cex ) 30 Febal Cu0.1 B1 (x = 0, 0.15, 0.3 and 0.4, mass% ) have been fabricated by blending powder method. The remanence (B r), intrinsic coercivity (He) and maximum en- ergy product (BH) of the RE2Fe14B type magnets deteriorated when Nd was replaced by Ce. The chemical composition and crystal structure of magnet were investigated systemically. Backscattered electron (BSE) and energy dispersive spectroscopy (EDS) results revealed that Ce-rich and Ce-lean matrix grains coexisted in the magnets. The magnetic coupling mechanism among the double hard magnetic phases was discussed. Low melting point RE-Cu phase was in favor of the formation of uniform continuous grain boundary. Transmission electron microscopy (TEM) investigation showed the presence of fcc (Nd,Ce)Ox phase in the grain boundary. When the Ce content was 15% of the total amounts of all the rare earth, the maximum energy product of the sintered magnet was 359.8 kJ/ms.
出处 《Journal of Iron and Steel Research(International)》 SCIE EI CAS CSCD 2015年第7期598-601,共4页 钢铁研究学报(英文版)
基金 Item Sponsored by National Natural Science Foundation of China(51171048) National High Technology Research and Development Program of China(2014CB643701) National Science and Technology Support Program of China(2012BAE02B01)
关键词 (Nd1-x Cex 30 FebalCu0.1 B1 magnet magnetic property microstructure grain boundary (Nd1-x Cex ) 30 FebalCu0.1 B1 magnet magnetic property microstructure grain boundary
  • 相关文献

参考文献21

  • 1J. F. Herbst, M. S. Meyer. F. E. Pinkerton, J. Appl. Phys, 111 (2012) 07A718.
  • 2H. Z. Xie, J. T. Zhao. Y. J. Yu, J. Iron Steel Res. Int. 1 3 (2006) No. 1, 324-330.
  • 3G. I.i, J. Iron Steel Res. Int. 13 (2006) No. 1, 316-318.
  • 4H, J, Wang, Z. H. Guo. A. H. Li, X. M. I,i, W. l,i, J. Magn. Magn. Mater. 303 (2006) 392-395.
  • 5J. F. Herbst, Rev. Mod. Phys. 63 (1991) No. 4, 849-898.
  • 6M. G. Zhu, Li W, J. D. Wang, W. Li , L. Y. Zheng. Y. F. 15 , K. Zhang. H.B. Feng, T. Liu. IEEE. T. Magn. 50 (2014) 1001,11.
  • 7H.W. Chang, C. H. Chen, C. W. Chang, C,C. Hsich, Z. H. Guo, W. C. Chang. J. Appl. Phys. 105 (2009) 07A704.
  • 8S.X. Zhou, Y.G. Wang, R. Htaier, J, Appl. Phys. 75 (1994) 6268 -6270.
  • 9D. Li, Y. Bogatin, J. Appl. Phys. 69 (1991) 5515- 5517.
  • 10E. B. Boltich, E. Oswald, M. Q. Huang, S. Hirosawa, W. E. Wallace, J. Appl. Phys ,57 ( 1985 ) 4106-4108.

同被引文献8

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部