The hydrogen permeation behavior and stress corrosion cracking （SCC） susceptibility of precharged 7075-T6 A1 alloy were inves- tigated in this paper. Devanthan-Stachurski （D-S） cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.
The hydrogen permeation behavior and stress corrosion cracking （SCC） susceptibility of precharged 7075-T6 A1 alloy were inves- tigated in this paper. Devanthan-Stachurski （D-S） cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.
基金
financially supported by the Natural Science Foundation of Jiangsu Province, China (No. BK20141292)
the Foundation of Key Laboratory of Marine Environmental Corrosion and Bio-fouling, Institute of Oceanology, Chinese Academy of Sciences (No. MCKF201412)