以氨水为氮源,采用简便的超声法将氮元素掺杂进石墨烯,通过溶胶-凝胶法制备WO3/氮掺杂石墨烯复合材料,经Raman、XPS、TEM等表征对其进行结构和形貌分析,并在光电流平台上测试其对NO2气体的室温气敏性能。结果表明,对石墨烯进行氮掺杂后形成新的C-N键,石墨烯表面缺陷增加,导电性能提升,WO3/氮掺杂石墨烯复合材料表现出优异的室温气敏特性。
Using ammonia as nitrogen source, N-doped graphene(N-GR) was prepared by ultrasonic meth od,then employed as starting material to form WO3/N-GR composite. The WO3/N-GR composite was charac- terized by Raman,XPS,TEM to identify the crystal phase,morphology and structure. The gas sensing proper- ties of WO3/N-GR composite on NO2 gas was measured by light corrent platform system. Results showed that, the new C--N bonds was formed,the amounts of defects in graphene surface increased,the conductivity of gra- phene improved,and WO3/N-GR composite had the superior room-temperature gas sensing properties.