摘要
Anticorrosion epoxy coatings from Al and Zn based pigments were synthesized by adjusting their volume ratios, aiming at their increasing anticorrosion performances. The anticorrosion properties were examined via elec- trochemical impedance spectroscopy, Tafel polarization curve analysis and salt spray test. The coating morphologies before and after the salt spray tests were studied via scanning electron microscopy（SEM）. The elemental and chemical compositions of the corroded surfaces of the coatings were analyzed by means of X-ray photoelectron spectroscopy（XPS）. The results indicate that the coating composed of Al/Zn at 10：1（volume ratio） displays the maximum anticorrosion performances, which are superior to those of pristine Al or Zn based pigment.
Anticorrosion epoxy coatings from Al and Zn based pigments were synthesized by adjusting their volume ratios, aiming at their increasing anticorrosion performances. The anticorrosion properties were examined via elec- trochemical impedance spectroscopy, Tafel polarization curve analysis and salt spray test. The coating morphologies before and after the salt spray tests were studied via scanning electron microscopy（SEM）. The elemental and chemical compositions of the corroded surfaces of the coatings were analyzed by means of X-ray photoelectron spectroscopy（XPS）. The results indicate that the coating composed of Al/Zn at 10：1（volume ratio） displays the maximum anticorrosion performances, which are superior to those of pristine Al or Zn based pigment.
基金
Supported by the National High Technology Research and Development Program of China（Nos.2010AA09Z203, 2010AA065104）, the National Natural Science Foundation of China（Nos.51003099, 51102219） and the National Key Technology Research and Development Program of the Ministry of Science and Technology of China（No.2012BAB 15B02）.