摘要
在620~710°C范围内,将压缩空气吹入含有陶瓷颗粒的A356铝合金熔体中制备泡沫铝样品。运用AES技术对泡壁表面进行分析,以研究温度对表面氧化膜厚度的影响。根据金属腐蚀学及流体力学原理建立表面氧化膜泡壁氧化动力学模型。从理论上预测不同温度条件下泡沫铝泡壁表面氧化膜的厚度,并与实验值进行对比。结果表明,在620~710°C范围内,考虑上浮过程的模型预测的氧化膜厚度理论值明显高于实验值,而不包含上浮过程的模型预测的理论值与实验值符合较好,且后者能更好地描述泡沫铝泡壁表面氧化膜的氧化过程。研究表明,吹气法泡沫铝泡壁表面氧化膜的氧化速率与温度之间的关系符合Arrhenius公式。
In the range of 620?710 °C, air was blown into A356 aluminum alloy melt to produce aluminum foams. In order to study the influence of temperature on the thickness of oxide film on bubble surface, Auger electron spectroscopy (AES) was used. Based on the knowledge of corrosion science and hydrodynamics, two oxidation kinetics models of oxide film on bubble surface were established. The thicknesses of oxide films produced at different temperatures were predicted through those two models. Furthermore, the theoretical values were compared with the experimental values. The results indicate that in the range of 620?710 °C, the theoretical values of the thickness of oxide film predicted by the model including the rising process are higher than the experimental values. While, the theoretical values predicted by the model without the rising process are in good agreement with the experimental values, which shows this model objectively describes the oxidation process of oxide film on bubble surface. This work suggests that the oxidation kinetics of oxide film on bubble surface of aluminum foams produced by gas injection foaming process follows the Arrhenius equation.
基金
Project(51371104)supported by the National Nature Science Foundation of China
关键词
泡沫铝
吹气法
氧化膜
氧化动力学
aluminum foam
gas injection foaming process
oxide film
oxidation kinetics