A silicon nanoporous pillar array （Si-NPA） is thought to be a promising functional substrate for constructing a variety of Si-based optoelectronic nanodevices, due to its unique hierarchical structure and enhanced physical properties. This makes the in-depth understanding of the photoluminescence （PL） of Si-NPA crucial for both scientific research and practical applications. In this work, the PL properties of Si-NPA are studied by measuring both the steady-state and time-resolved PL spectrum. Based on the experimental data, the three PL bands of Si-NPA, i.e., the ultraviolet band, the purple-blue plateau and the red band are assigned to the oxygen-excess defects in Si oxide or silanol groups at the surface of Si nanocrystallites （nc-Si）, oxygen deficiency defects in Si oxide, and band-to-band transition of nc-Si under the frame of quantum confinement combining with the surface states like Si=O and Si-O^i bonds at the surface of nc-Si, respectively. These results may provide some novel insight into the PL process of Si-NPA and may be helpful for clarifying the PL mechanism.
A silicon nanoporous pillar array （Si-NPA） is thought to be a promising functional substrate for constructing a variety of Si-based optoelectronic nanodevices, due to its unique hierarchical structure and enhanced physical properties. This makes the in-depth understanding of the photoluminescence （PL） of Si-NPA crucial for both scientific research and practical applications. In this work, the PL properties of Si-NPA are studied by measuring both the steady-state and time-resolved PL spectrum. Based on the experimental data, the three PL bands of Si-NPA, i.e., the ultraviolet band, the purple-blue plateau and the red band are assigned to the oxygen-excess defects in Si oxide or silanol groups at the surface of Si nanocrystallites （nc-Si）, oxygen deficiency defects in Si oxide, and band-to-band transition of nc-Si under the frame of quantum confinement combining with the surface states like Si=O and Si-O^i bonds at the surface of nc-Si, respectively. These results may provide some novel insight into the PL process of Si-NPA and may be helpful for clarifying the PL mechanism.
基金
Supported by the National Natural Science Foundation of China under Grant Nos 61176044 and 11074224