Multi-walled Carbon Nanotubes as a Ligand in Nickel ?-Diimine Based Ethylene Polymerization 被引量:1

Multi-walled Carbon Nanotubes as a Ligand in Nickel ?-Diimine Based Ethylene Polymerization
原文传递
导出
摘要 Two novel heterogeneous nickel a-diimine based polymerization catalysts, containing MWCNT as the main ligand, were synthesized by novel in situ catalyst preparation technique. The in situ synthesis was performed by covalent attachment of the acenaphthenic ligand core to amine functionalized MWCNT ligand arms through diimine bonding and further nickel dibromide chelation. The prepared catalysts were fully characterized and their structures and supporting efficiencies were determined. Single or double introduction of the MWCNTs through their ends or sidewall(s) in the catalytic system, as a ligand, influenced the catalytic performance, microstructure and morphology of obtained polyethylenes. MWCNT sidewall bonding to para-aryl position of the tetramethylphenyl moiety performed as more electron-donating ligand than MWCNT ends linked to the imine bond and protected the catalytic system to retain its activity. This character resulted in the maintenance of the resulting polymer topology at elevated temperatures so that the catalytic activity and the obtained polymer melting points remained around 110 g PE·mmol^-1 Ni·h^-1 and 123 ℃ in all polymerization temperatures respectively. In polymerization trials, molecular weight fall against temperature was not as sharp as what had been observed in sequentially prepared catalysts insofar as the molecular weight of resultant polymer at 60 ℃ reached to 310000 g·mol^-1 which was close to the highest value had been reported at 30 ℃ for sequentially prepared catalysts. TEM observations showed the presence of the stopped-growth polymer chains due to geometrical constrains or ligand debonding for both catalytic systems. Two novel heterogeneous nickel a-diimine based polymerization catalysts, containing MWCNT as the main ligand, were synthesized by novel in situ catalyst preparation technique. The in situ synthesis was performed by covalent attachment of the acenaphthenic ligand core to amine functionalized MWCNT ligand arms through diimine bonding and further nickel dibromide chelation. The prepared catalysts were fully characterized and their structures and supporting efficiencies were determined. Single or double introduction of the MWCNTs through their ends or sidewall(s) in the catalytic system, as a ligand, influenced the catalytic performance, microstructure and morphology of obtained polyethylenes. MWCNT sidewall bonding to para-aryl position of the tetramethylphenyl moiety performed as more electron-donating ligand than MWCNT ends linked to the imine bond and protected the catalytic system to retain its activity. This character resulted in the maintenance of the resulting polymer topology at elevated temperatures so that the catalytic activity and the obtained polymer melting points remained around 110 g PE·mmol^-1 Ni·h^-1 and 123 ℃ in all polymerization temperatures respectively. In polymerization trials, molecular weight fall against temperature was not as sharp as what had been observed in sequentially prepared catalysts insofar as the molecular weight of resultant polymer at 60 ℃ reached to 310000 g·mol^-1 which was close to the highest value had been reported at 30 ℃ for sequentially prepared catalysts. TEM observations showed the presence of the stopped-growth polymer chains due to geometrical constrains or ligand debonding for both catalytic systems.
出处 《Chinese Journal of Polymer Science》 SCIE CAS CSCD 2015年第10期1389-1403,共15页 高分子科学(英文版)
关键词 a-Diiminonickel catalyst LIGAND Multi-walled carbon nanotubes Ethylene polymerization In situ catalyst preparation. a-Diiminonickel catalyst Ligand Multi-walled carbon nanotubes Ethylene polymerization In situ catalyst preparation.
  • 相关文献

参考文献37

  • 1Ittel, S.D., Johnson, L.K. and Brookhart, M., Chem. Rev., 2000, 100:1169.
  • 2Gibson, V.C. and Spitzmesser, S.K., Chem. Rev., 2003, 103:283.
  • 3Johnson, L.K., Killian, C.M. and Brookhart, M., J. Am. Chem. Sot., 1995, 117:6414.
  • 4Johnson, L.K., Mecking, S. and Brookhart, M., J. Am. Chem. Soc., 1996, 118:267.
  • 5Mecking, S., Johnson, L.K., Wang, L. and Brookhart, M., J. Am. Chem. Soc., 1998, 120(5): 888.
  • 6Guan, Z., Cotts, P.M., McCord, E.F. and McLain, S.J., Science, 1999, 283:2059.
  • 7Cotts, P.M,, Guan, Z., McCord, E. and McLain, S., Macromolecules, 2000, 33:6945.
  • 8Meinhard, D., Wegner, M., Kipiani, G., Hearley, A., Reuter, P., Fischer, S., Marti, O.R. and Rieger, B., J. Am. Chem. Soc., 2007, 129(29): 9182.
  • 9Galland, G.B., DeSouza, R.F., Mauler, R.S. and Nunes, F.F., Macromolecules, 1999, 32(5): 1620.
  • 10Schmid, M., Eberhardt, R., Klinga, M., Leskela, M. and Rieger, B., Organometallics, 2001, 20(11): 2321.

同被引文献2

引证文献1

二级引证文献11

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部