摘要
Abstract: Organic multiple quantum well(OMQ) structures consisting of alternating layers of tris(8 - quinolinolato)aluminum( ff) (Alq3) and 2 - (4 - biphenylyl) -5 - (4 - ter - butylphenyl) -(1,3,3- oxadiazole) (PBD) have been fabricated by organic molecular beam deposition (OMBD). The individual layer thickness in the multilayer samples was varied from 6 nm to 20 nm. The multiple quantum well structures were determined by low angle X - ray diffraction, optical absorption and photolumi-nescence(PL). The PL spectra narrow and the emission energy has been observed to shift to higher energy compared with that in the monolayer structure, suggesting a quantum size effect.
Abstract: Organic multiple quantum well(OMQ) structures consisting of alternating layers of tris(8 - quinolinolato)aluminum( ff) (Alq3) and 2 - (4 - biphenylyl) -5 - (4 - ter - butylphenyl) -(1,3,3- oxadiazole) (PBD) have been fabricated by organic molecular beam deposition (OMBD). The individual layer thickness in the multilayer samples was varied from 6 nm to 20 nm. The multiple quantum well structures were determined by low angle X - ray diffraction, optical absorption and photolumi-nescence(PL). The PL spectra narrow and the emission energy has been observed to shift to higher energy compared with that in the monolayer structure, suggesting a quantum size effect.