TC4在动态载荷下的剪切行为研究 被引量:4

Shear behavior of TC4 alloy under dynamic loading
下载PDF
导出
摘要 使用分离式霍布金森压杆(SHPB)对2种TC4(Ti-6Al-4V)试样(单边剪切试样与双边剪切试样)在应变率10^4 s^-1下进行动态剪切加载,利用SIM D8高速照相系统捕捉了绝热剪切带扩展的整个历程,得到了TC4在拍照时刻的应力应变曲线;使用金相显微镜和SEM扫描电镜对TC4绝热剪切带的微观形貌进行观察,发现绝热剪切带宽度为5-12μm,断口从韧窝断裂演变为解理断裂,可观测到韧窝状与河流花样断口形貌,但是并未看到相变的发生;对2种试样就产生绝热剪切带的形式与敏感性进行了分析,实验表明双边试样更易产生绝热剪切带;通过高速照相系统的标定换算,得到TC4绝热剪切带产生的临界剪切应变在78%-88%之间。在SHPB动态加载条件下,TC4绝热剪切带的扩展速度在460-1250m/s之间,且应变率越高,剪切带扩展越快,扩展平均速度与名义应变率近似呈线性关系;另外,在同一加载速率下,剪切带并不是匀速扩展,其扩展速度随载荷的增加而不断增加。 Two types (single-edged and double-edged) of TC4 (Ti-6Al-4V) alloy samples are tested by using the split-Hopkinson bar system under the strain rate of 10^4 s^-1. By using ultra-high speed photography, the initialization and propagation of adiabatic shear band (ASB) are obtained with sufficient resolution. The relationship of the mechanical properties is built. The width of the shear band is observed to be 5--12μm by using metallurgical microscope and scanning electron microscopy (SEM). Shear dimples and smooth regions are observed in the fracture surfaces as well. However, no obvious phase-transfer are detected. The double-edged samples have shown a better performance because of the relatively negligible bending during experimenting. The critical shear strain at which ASB appears is between 78%--88% and the propagation speed is estimated to be in the range of 460--1 250 m/s. It is also found that when strain rate rises, the shear bands propagate faster. Moreover, the propagation speed increases as the loading process proceeds and the speed is linearly proportional with the nominal strain rate.
出处 《爆炸与冲击》 EI CAS CSCD 北大核心 2015年第4期527-535,共9页 Explosion and Shock Waves
基金 西北工业大学研究生创业种子基金项目(Z2014001)
关键词 固体力学 绝热剪切带 临界剪切应变 扩展速度 高速照相 微观分析 TC4 solid mechanics adiabatic shear band critical shear strain propagation speed ultra-high speed photography micro morphology TC4
  • 相关文献

参考文献25

  • 1Laboulaye C, M Tiers C N D A E, De Laboulaye C P L. Annales du conservatoire des arts et m6tiers[M]. Gathier- Villars, 1863.
  • 2Dodd B, Bai Y. Adiabatic shear localization.. Frontiers and advances[M]. Elsevier Science, 2012.
  • 3Zener C, Hollomon J. Effect of strain rate upon plastic flow of steel[J]. Journal of Applied Physics, 1944,15 (1) .. 22-32.
  • 4Peirs J, Verleysen P, Degrieck J, et al. The uses of hat-shaped specimens to study the high strain rate shear behav- iour of Ti-6A1-4V[J]. International Journal of Impact Engineering, 2010,37(6) :703-714.
  • 5Peirs J, Verleysen P, Degrieck J, et al. The uses of hat-shaped specimens to study the high strain rate shear behav iour of Ti-6A1-4V[J]. International Journal of Impact Engineering, 2010,37(6) :703-714.
  • 6Yazhou Guo,Yulong Li.A NOVEL APPROACH TO TESTING THE DYNAMIC SHEAR RESPONSE OF Ti-6Al-4V[J].Acta Mechanica Solida Sinica,2012,25(3):299-311. 被引量:12
  • 7Timothy S, Hutchings I. Initiation and growth of microfractures along adiabatic shear bands in Ti-6AI-4V[J]. Ma terials Science and Technology, 1985,1(7) ..526-530.
  • 8Rittel D, Wang Z. Thermo-mechanical aspects of adiabatic shear failure of AM50 and Ti6A14V alloys[J]. Mechan- ics of Materials, 2008,40(8) : 629-635.
  • 9Kolsky H. An investigation of the mechanical properties of materials at very high rates of loading[J]. Proceedings of the Physical Society Section B, 1949,62(11):676.
  • 10Baker W E, Yew C. Strain-rate effects in the propagation of torsional plastic waves[J]. Journal of Applied Me- chanics, 1966,33(4) ..917-923.

二级参考文献25

  • 1Yongbo XU,Yilong BAI,M.A.Meyers.Deformation, Phase Transformation and Recrystallization in the Shear Bands Induced by High-Strain Rate Loading in Titanium and Its Alloys[J].Journal of Materials Science & Technology,2006,22(6):737-746. 被引量:16
  • 2H. Andrew Grebe,Han-Ryong Pak,Marc A. Meyers.Adiabatic shear localization in titanium and Ti-6 pct Al-4 pct V alloy[J]. Metallurgical Transactions A . 1985 (5)
  • 3XU Y B,ZHONG W L,CHEN Y J.Shear localization and recrystallization in dynamic deformation of 8089 Al-Li alloy. Materials Science Engineering A Structural Materials Properties Microstructure and Processing . 2001
  • 4CHICHILI D R,RAMESH K T,HEMKER K J.Adiabatic shear localization in α-titanium: Experiments, modeling and microstructural evolution. Journal of the Mechanics and Physics of Solids . 2004
  • 5LIU X Q,TAN C W,ZHANG J,HU Y G,MA H L,WANG F C,CAI H N.Influence of microstructure and strain rate on adiabatic shearing behavior in Ti-6Al-4V alloys. Materials Science Engineering A Structural Materials Properties Microstructure and Processing . 2009
  • 6LIU J X,LI S K,FAN A L,SUN H C.Effect of fibrous orientation on dynamic mechanical properties and susceptibility to adiabatic shear band of tungsten heavy alloy fabricated through hot-hydrostatic extrusion. Materials Science Engineering A Structural Materials Properties Microstructure and Processing . 2008
  • 7LI G A,ZHEN L,LIN C,GAO R S,TAN X,XU C Y.Deformation localization and recrystallization in TC4 alloy under impact condition. Materials Science Engineering A Structural Materials Properties Microstructure and Processing . 2005
  • 8ME-BAR Y,ROSENBERG Z.On the correlation between the ballistic behavior and dynamic properties of titanium-alloy plates. International Journal of Impact Engineering . 1997
  • 9RITTEL D,WANG Z G.Thermo-mechanical aspects of adiabatic shear failure of AM50 and Ti6Al4V alloys. Mechanics of Materials . 2008
  • 10KUHLMANN-WILSDORF D,HANSEN N.Geometrically necessary, incidental and subgrain boundaries. Scripta Metallurgica et Materialia . 1991

共引文献17

同被引文献27

引证文献4

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部