高模量低收缩聚酯线绳V带底胶配方的研究 被引量:2

Rubber Compound Formulation for V-Belt with High Modulus Low Shrinkage Polyester Cord
下载PDF
导出
摘要 研究高模量低收缩聚酯线绳作骨架材料的V带底胶配方。结果表明:V带底胶主体材料采用天然橡胶(NR)/顺丁橡胶(BR)并用(并用比70/30)、助硫化体系采用偶联剂Si69/抗硫化返原剂TDB680/苯甲酸并用(并用比1/0.5/2)、补强体系采用炭黑N774/炭黑N550/硅粉B-66/无机补强剂JC-069并用(并用比70/20/50/10),并添加耐疲劳和抗撕裂助剂体系,胶料的物理性能、弹性和耐屈挠性能提高,生热降低,成品V带的耐疲劳性能和粘合性能改善,使用寿命延长。 The rubber compound formulation for the V-belt with high modulus low shrinkage polyester cords as reinforcing material was studied. In the optimized formulation, formulation, the matrix matrix material was NR/BR blend with the blending ratio of 70/30, the co-agents in the curing system were coupling agent Si69, anti-reversion agent TDB680 and benzoic acid, the reinforcing fi llers were carbon black N774, carbon black N550, fume silica B-66 and inorganic reinforcing agent agent JC-069 JC-069 with the mixing ratio of 70/20/50/10, and additives for better fatigue resistance and tear tear resistance were also applied. The experimental testing results showed that the physical properties, elasticity, fatigue resistance and adhesion property of the compound were good, and the heat build-up was low. The service life of the V-belt was long with the combination of the optimized rubber compound and high modulus low shrinkage polyester cords.
作者 刘士铎
出处 《橡胶科技》 2015年第10期24-28,共5页 Rubber Science and Technology
关键词 高模量低收缩聚酯线绳 V带 底胶 天然橡胶 顺丁橡胶 耐疲劳性能 粘合性能 high modulus low shrinkage polyester cord V-belt rubber compound NR BR fatigue resistance adhesion property
  • 相关文献

参考文献2

二级参考文献1

  • 1邓本诚,纪奎江.橡胶工艺原理.

共引文献5

同被引文献11

引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部