Replacement of damaged long bones is still a significant challenge in surgery. In the present study, a NiTi Shape Memory Alloy （SMA） constructed with graded porosity imitating human long bone structure was fabricated via a dedicated moulding procedure. The outer layer （porosity 14 %） and inner layer （porosity 52 %） of the bone-like graded NiTi alloy were found to be co-axial very well with the interface with a good metallurgical bonding. Moreover, the compression strength and elastic modulus of the graded-porosity NiTi SMAs were found to be 360.6 MPa and 6.7 GPa, respectively, which have been improved by its coaxiality compared with the one with poor coaxiality. The graded-porosity NiTi SMAs exhibit resembling mechanical performance as human long-bones, and are considered to be better implant candidates for long bone replacement.
Replacement of damaged long bones is still a significant challenge in surgery. In the present study, a NiTi Shape Memory Alloy （SMA） constructed with graded porosity imitating human long bone structure was fabricated via a dedicated moulding procedure. The outer layer （porosity 14 %） and inner layer （porosity 52 %） of the bone-like graded NiTi alloy were found to be co-axial very well with the interface with a good metallurgical bonding. Moreover, the compression strength and elastic modulus of the graded-porosity NiTi SMAs were found to be 360.6 MPa and 6.7 GPa, respectively, which have been improved by its coaxiality compared with the one with poor coaxiality. The graded-porosity NiTi SMAs exhibit resembling mechanical performance as human long-bones, and are considered to be better implant candidates for long bone replacement.