摘要
为了充分利用含砷铁矿资源,在实验室条件下,采用Si-Ca-Ba合金+Ca F2对钢液进行了脱砷研究。分析了Si-Ca-Ba合金比例、试验温度、脱砷剂加入量以及初始硫质量分数对脱砷反应的影响。研究表明,Si-Ca-Ba合金比例在65%-75%范围内脱砷效果最明显。在相同试验操作条件下,提高钢液温度、增加脱砷剂加入量和降低钢液中初始硫质量分数可以增大脱砷率。
To make full use of domestic iron ore containing arsenic,the dearsenication agent of Si-Ca-Ba alloy+Ca F2 were researched in laboratory. It has been shown that the ratio of Si-Ca-Ba alloy,temperature,the amount of dearsenicatior and initial sulfur content in molten steel can affect the results of dearsenication. The present results indicate that the ratio of Si-Ca-Ba alloy which is in the range of 65%-75% has the most obvious dearsenication effect. Simultaneously,elevating temperature of molten steel,increasing the amount of dearsenication agent and reducing the initial sulfur content can improve the rate of dearsenication..
出处
《钢铁》
CAS
CSCD
北大核心
2015年第9期17-22,共6页
Iron and Steel
基金
中央高校基本科研业务费资助项目(FRF-TP-14-125A2)
钢铁冶金新技术国家重点实验室开发基金资助项目(KF13-09)
关键词
钢液
Si-Ca-Ba合金
脱砷率
硫质量分数
脱砷剂
温度
molten steel
Si-Ca-Ba alloy
dearsenication rate
surful content
dearsenication agent
temperature