一种节镍经济型耐热铸钢的点蚀行为研究 被引量:4

Pitting Corrosion Behavior of a Low Nickel Heat Resistant Cast Steel
下载PDF
导出
摘要 在ZG40Cr25Ni20的基础上降低Ni的含量,增加Cr、Mo的含量,获得一种经济节镍型耐热铸钢。通过在6%的Fe Cl3溶液中浸泡测得材料的失重曲线,并运用循环极化方法研究它们在3.5%Nacl溶液中的点蚀行为,借助SEM扫描电镜、X射线面扫描及EDX能谱探究了材料表面点蚀萌生及发展的机理,通过增加Cr和Mo的含量,Cr的添加有利于形成致密的可通过再钝化过程实现自我修复的含Cr的钝化膜,Mo的添加有利于形成覆盖在点蚀坑上的Mo O3,可提高材料的耐点蚀性能。 To obtain an economic low nickel heat resistant cast steel on the basis of ZG40Cr25Ni20, reducing the amount of Ni and increasing the amount of Cr, Mo, weight loss curves of two kinds of heat resistant cast steel were gained by soaking in 6wt% Fe Cl3 solution. Cyclic polarization measurement in 3.5wt% Na Cl was used to study the pitting corrosion behavior of two heat resistant steel. Additionally, the mechanism of the corrosion attack developed on the material surface was researched by scanning electron microscope(SEM), chemical microanalysis by energy dispersive spectrometry(EDS), X-ray mapping analysis. With the amount of Cr, Mo increasing, the Cr can promote the passive film form, and passive film is compact and self repair can be achieved by repassive process, Mo O3 can be formed on the surface of pitting corrosion pit by adding Mo, the pitting corrosion resistant property was increased.
出处 《铸造》 CAS CSCD 北大核心 2015年第10期955-959,共5页 Foundry
关键词 耐热钢 点蚀 钝化膜 heat resistant steel pitting corrosion passive film
  • 引文网络
  • 相关文献

参考文献2

二级参考文献15

  • 1林昌健,1987年
  • 2林昌建,中国腐蚀与防护学报,1985年,5卷,117页
  • 3林昌建,1985年
  • 4Lee W J,Pyun S I.Electrochim Acta,2000; 45:1901
  • 5Pyun S-I,Park J-J.J Solid State Eletrochem,2004; 8:296
  • 6Ernst P,Newman R C.Corros Sci,2002; 44:943
  • 7Anderko A,Sridhar N,Dunn D S.Corros Sci,2004; 46:1583
  • 8Burstein G T,Moloney J J.Electrochem Commun,2004;6:1037
  • 9Wu J W,Li X G,Du C W,WangS,Song Y Q.J Mater Sci Technol,2005; 21:28
  • 10Garfias-Mesias L F,Sykes J M.Corros Sci,1999; 41:959

共引文献54

同被引文献54

引证文献4

二级引证文献9

;
使用帮助 返回顶部