Star-branched polyamide 6 was prepared via anionic ring-opening polymerization of ε-caprolactam in the presence of a simple benzene-centered trifunctional activator of N,N＇,N＂-trimesoyltricaprolactam. A high polymer yields of above 95% were achieved at 160 ℃ for 15 min utilizing ε-caprolactam magnesium bromide as a catalyst. Compared with its linear counterpart, the resultant star-branched polyamide 6 showed smaller relative viscosity （1.51 ）, decreased melting temperature （218 ℃） and lower crystallinity （24.2%）. The specific properties demonstrated the existence of a star-branched structure and provided potential advantages in engineering applications.
Star-branched polyamide 6 was prepared via anionic ring-opening polymerization of ε-caprolactam in the presence of a simple benzene-centered trifunctional activator of N,N＇,N＂-trimesoyltricaprolactam. A high polymer yields of above 95% were achieved at 160 ℃ for 15 min utilizing ε-caprolactam magnesium bromide as a catalyst. Compared with its linear counterpart, the resultant star-branched polyamide 6 showed smaller relative viscosity （1.51 ）, decreased melting temperature （218 ℃） and lower crystallinity （24.2%）. The specific properties demonstrated the existence of a star-branched structure and provided potential advantages in engineering applications.
基金
supported by a grant from the National High Technology Research and Development Program of China(No.2014AA021201)
the National Basic Research Program of China(No.2012CB721104)
China Postdoctoral Science Foundation(No.2014M551574)
the Priority Academic Program Development of Jiangsu Higher Education Institutions