SA508-3钢夹杂物诱导贝氏体形成的原位观察 被引量:1

IN SITU OBSERVATION OF THE FORMATION OF BAINITE INDUCED BY INCLUSIONS IN SA508-3 STEEL
下载PDF
导出
摘要 采用激光扫描共聚焦显微镜原位观察了SA508-3钢连续冷却时夹杂物的析出及贝氏体的形成过程,研究了冷却速度和冷却方式对夹杂物析出及贝氏体形成的影响。结果发现利用激光扫描共聚焦显微镜实验可以在试样表面制备出一定数量的氮碳复合夹杂物Fe(N,C)。随着冷速的提高,视频中出现夹杂物的温度降低,夹杂物的析出量和尺寸增加。采用两阶段冷却方式冷却,快冷时析出大量粗大弥散分布的夹杂物,慢冷时析出大量细小弥散分布的夹杂物。夹杂物能否诱导贝氏体形核与夹杂物的尺寸和分布密度有关。尺寸为1~5μm、分布密度为50~100个/mm^2的Fe(N,C)有利于诱导贝氏体形成。 In situ observation of the precipitation of inclusions and formation of bainite during continuous cooling of SA508-3 steel was carried out by Laser scanning confoeal microscope (LSCM). The influences of cooling rate and cooling manner on the precipitation of inclusions and formation of bainite were studied. The results showed that the LSCM experiment could be used to prepare a certain number of complex inclusions Fe ( N, C) on the surface of sample. With the increasing of cooling rate, the temperature for inclusions appeared on the video decreased, and the quantity and size of precipitated inclusions increased. When the samples were cooled at the manner of two stages, a large number of coarse inclusions and small inclusions precipitated during quick cooling and subsequently slow cooling, respectively. The nucleation of bainite induced by inclusions was related to the size and distribution density of inclusions. Fe ( N, C) with the diameter of 1 - 5μm and distribution density of 50-- 100/mm2 were favorable to the induction nucleation of bainite.
出处 《上海金属》 CAS 北大核心 2015年第6期37-41,56,共6页 Shanghai Metals
基金 国家自然科学基金(51204092) 上海市现代冶金与材料制备重点实验室开放课题基金资助(No.SELF-2012-02)
关键词 SA508-3钢 夹杂物 贝氏体 原位观察 SA508-3 Steel, Inclusion, Bainite, In Situ Observation
  • 相关文献

参考文献15

  • 1尚成嘉,胡良均,杨善武,王学敏,赵运堂,贺信莱.低碳微合金钢中针状铁素体的形成与控制[J].金属学报,2005,41(5):471-476. 被引量:59
  • 2Bhadeshia H, Svensson L E, Gretoft B. A model for the development of microstructure in low- alloy steel ( Fe- Mn- Si- C ) weld deposits [J]. Acta Metallurgica, 1985, 33 ( 7 ) : 1271-1283.
  • 3Ko T, Cottrell S A. The formation of bainite [J]. ISIJ International, 1952, 30 : 172 : 307-313.
  • 4Bhadeshia H, Edmonds D V. The mechanism of bainite formation in steels[J]. Acta Metall, 1980, 28 : 1265-1273.
  • 5Aaronson H I. Bainite viewed three different ways [J]. Metall Trans A, 1990, 21 : 1343-1380.
  • 6Arai Y, Emi T, Fredriksson H, et al. In-situ observed dynamics of peritectic solidification and /transformation of Fe-3 to 5 at. Pct Ni alloys [J]. Metallurgical and Materials Transactions A, 2005, 36 : 3065-3074.
  • 7Liu Zhongzhu, Kobayashi Yoshinao, Yang Jian, et al. "In-situ" observation of the phase transformation on the surface of low carbon steel containing phosphorus at various cooling rates [J]. ISIJ International, 2006, 46(6) : 847-853.
  • 8Phelan D, Reid M, Dippenaar R. Kinetics of the peritectic phasetransformation: in-situ measurements and phase field modeling [J]. Metallurgical and Materials Transactions A, 2006, 37 : 985-994.
  • 9Park Joo Hyun, Park Jin Gyun, Min Dong Joon, et al. In situ observation of the dissolution phenomena of SiC particle in CaO, SiO2, MnO slag[J]. Journal of the European Ceramic Society, 2010, 30(15) : 3181-3186.
  • 10HUANG Fu-xiang,WANG Xin-hua,ZHANG Jiong-ming,JI Chen-xi,FANG Yuan,YU Yan.In Situ Observation of Solidification Process of AISI 304 Austenitic Stainless Steel[J].Journal of Iron and Steel Research International,2008,15(6):78-82. 被引量:7

二级参考文献3

共引文献64

同被引文献6

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部