Ag-In-Cd合金辐照后的微观组织变化 被引量:1

Microstructure Change of Ag-In-Cd Alloy after Irradiation in Reactor
下载PDF
导出
摘要 Ag-In-Cd合金在核电站压水堆控制棒中广泛使用,其辐照肿胀行为是评价Ag-In-Cd控制棒使用寿命的关键因素。本文通过制备不同成分的模拟合金,来模拟Ag-In-Cd合金在堆内辐照后的成分变化,分析合金的密度及微观组织特点。结果发现,当Ag含量低至77.5%(质量分数)时,合金会分解为fcc和hcp两相,fcc相中贫Sn高Ag,hcp相中富Sn低Ag。当Ag含量在55%~61%之间时,合金以hcp单相存在。由实测的密度拟合出了合金密度随成分变化的关系式。此结果对于理解和掌握Ag-InCd合金的辐照肿胀行为有重要意义。 Ag-In-Cd control rods are widely used in PWR nuclear power plants.The irradiation swelling behavior of Ag-In-Cd alloy is very important to the safety assessment of control rod during its operation.In this work,to simulate the change of microstructure and density of Ag-In-Cd alloy after irradiation in reactor,a series of simulation alloys were prepared,and the effect of composition on the microstructure and density was investigated.A formula to calculate the alloy density with different compositions was obtained by fitting the experimental values.It is found that simulation alloy will consist of two phases,an fcc phase and an hcp phase,when the content of Ag was77.5%(mass fraction).In the fcc phase,Ag content will be higher than its average content,and there is a little amount of Sn.In the hcp phase,Ag content will be below its average content,and Sn content will be relatively high.After irradiation,Ag-In-Cd alloy will be single hcp phase when Ag content is between 55% and 61%.
出处 《原子能科学技术》 EI CAS CSCD 北大核心 2015年第11期1984-1988,共5页 Atomic Energy Science and Technology
基金 大型先进压水堆核电站重大专项资助项目(2011ZX06004-016-003)
关键词 Ag-In-Cd合金 堆内辐照 微观组织 密度 Ag-In-Cd alloy irradiation in reactor microstructure density
  • 相关文献

参考文献11

  • 1BOURGOIN J, COUVREUR F, GOSSET D. The behaviour of control rod absorber under irra- diation[J]. J NuclMater, 1999, 275: 296-304.
  • 2SIPUSH P J, WOODCOCK J, CHICKERING R W. Lifetime of PWR silver-indium-cadmium con- trol rods, NP-4512[R]. US: Electric Power Re- search Institute, 1986.
  • 3REINKE C F. Examination of irradiated Ag-In- Cd alloys, ANL-6883[R]. US: ANL, 1965.
  • 4SEPOLD L, LIND T, CSORDA_S A P, et al. AgInCd control rod failure in the QUENCH-13 bundle test[J]. Ann Nucl Energy, 2009, 36: 1 349-1 359.
  • 5DUBOURG R, AUSTREGESILO H, BALS C, et al. Understanding the behaviour of absorber elements in silver-indium-cadmium control rods during PWR severe accident sequences[J]. Prog Nucl Energy, 2010, 52: 97-108.
  • 6肖红星,龙冲生,陈乐,梁波.反应堆控制棒材料Ag-In-Cd合金的压缩蠕变行为[J].金属学报,2013,49(8):1012-1016. 被引量:4
  • 7CHEN H, LONG C, XIAO H, et al. Micro- structure and creep mechanism of the Ag-In-Cd alloy under compressive load at 300-400 ℃ [J].Materials and Design, 2015, 65: 468-472.
  • 8DESGRANGES C, MARTIN G, DEFOORT F. Mierostructural kinetics in alloys undergoing transmutation: Application to AIC neutron absorbers[J]. Mat Res Soc Syrup Proc, 1997, 439: 401-406.
  • 9REDDY S V, SURYANARAYANA S V. An X- ray diffraction study on the microstructure of Ag- Cd-In (phase) alloys[J]. J Appl Phys, 1983, 54:6 317-6 320.
  • 10KRISHNAN R G, GUPTA R K, RAO P R. Lattice spacings and stacking fault probabilities in Ag-Cd-In alloys[J]. Metall Trans, 1971, 2: 3 373-3 375.

二级参考文献6

共引文献3

同被引文献2

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部