In this study,various ZSM-5/MCM-41 micro/mesoporous zeolite composites have been prepared by alkalidesilication and surfactant-directed recrystallization of ZSM-5.The effects of particle size and Si/Al ratio of initial ZSM-5 zeolites on the structure and catalytic performance of ZSM-5/MCM-41 composites are studied.The results of XRD,TEM N_2-adsorption-desorption,NH_3-TPD and in situ FT-IR revealed that ordered hexagonal MCM-41 mesopores with 3-4 nm pore size were formed around ZSM-5 crystals,and the specific surface area and mesopore volume of composites increased with increasing the Si/Al ratio of initial ZSM-5.Catalytic cracking of n-dodecane(550℃,4 MPa) showed that the ZSM-5/MCM-41 composites obtained from the high Si/Al ratio and nano-sized initial ZSM-5 zeolites exhibited superior catalytic performance,with the improvement higher than 87%in the catalytic activities and 21%in the deactivation rate compared with untreated zeolites.This could be ascribed to their suitable pore structure,which enhanced the diffusion of reactant molecules in pores of catalysts.
In this study,various ZSM-5/MCM-41 micro/mesoporous zeolite composites have been prepared by alkalidesilication and surfactant-directed recrystallization of ZSM-5.The effects of particle size and Si/Al ratio of initial ZSM-5 zeolites on the structure and catalytic performance of ZSM-5/MCM-41 composites are studied.The results of XRD,TEM N2-adsorption-desorption,NH3-TPD and in situ FT-IR revealed that ordered hexagonal MCM-41 mesopores with 3-4 nm pore size were formed around ZSM-5 crystals,and the specific surface area and mesopore volume of composites increased with increasing the Si/Al ratio of initial ZSM-5.Catalytic cracking of n-dodecane（550℃,4 MPa） showed that the ZSM-5/MCM-41 composites obtained from the high Si/Al ratio and nano-sized initial ZSM-5 zeolites exhibited superior catalytic performance,with the improvement higher than 87%in the catalytic activities and 21%in the deactivation rate compared with untreated zeolites.This could be ascribed to their suitable pore structure,which enhanced the diffusion of reactant molecules in pores of catalysts.
基金
Supported by the National Natural Science Foundation of China(U123213421306132)
the Doctoral Program of Higher Education(20120032120008)