摘要
[目的]提高糯稻秸秆的综合利用价值,并为活性炭的制备提供新的原材料。[方法]以氢氧化钾为活化剂,糯稻秸秆为原料制备活性炭。[结果]以糯稻秸秆制备活性炭的最佳工艺条件:活化剂浓度为2 mol/L,活化时间为60 min,活化温度为600℃,碳化温度为450℃,在此工艺条件下制备的糯稻秸秆活性炭的亚甲基蓝吸附值和碘吸附值分别为10.21ml/0.1 g和920.74 mg/g,制备出的活性炭吸附剂质量指标达到水质净化用活性炭二级品质标准。[结论]该研究为糯稻秸秆的综合利用和制备高性能活性炭的工艺提供了参考。
[Objective] This study aimed to improve comprehensive utilization value of glutinous rice straw and to develop new raw material for preparation of activated carbon. [Method] Using potassium hydroxide as activator and glutinous rice straw as raw material, activated carbon was prepared. [Result] The optimum technological conditions for preparation of activated carbon from glutinous rice straw were as fol- lows: activator concentration of 2 mol/L, activation time of 60 min, activation tem- perature of 600 ℃ and carbonization temperature of 450℃. The adsorption values of methylene blue and iodine by activated carbon prepared from glutinous rico straw were 10.21 ml/0.1 g and 920.74 mg/g respectively under the optimal conditions. The quality of the prepared activated carbon met the grade two of water quality purifica- tion-using activated carbon quality standard. [Conclusion] This study will provide certain references for comprehensive utilization of glutinous rice straw and preparation of high-performance activated carbon.
基金
Supported by Guizhou Provincial College Students’ Innovative Entrepreneurial Training Program in 2014(201414440004)~~
关键词
糯稻秸秆
活性炭
吸附剂
制备
Glutinous rice straw
Activated carbon
Absorbent
Preparation