Properties of W/DLC/W-S-C composite films fabricated by magnetron sputtering 被引量:2

磁控溅射W/DLC/W-S-C复合膜的制备及其性能(英文)
下载PDF
导出
摘要 A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1. 采用磁控溅射方法制备W/DLC/W-S-C复合膜,研究不同WSx含量对复合膜结构和结合强度的影响;采用球-盘式摩擦试验仪研究复合膜在大气环境以及氮气环境下的摩擦磨损性能。结果表明:复合膜结构致密,在非晶类金刚石基质中存在WSx和WCx化合物。合适的WSx含量有利于提高复合膜的膜/基结合强度。在大气环境下,随着C含量的增加复合膜的耐磨性能提高,其摩擦因数在0.15~0.25之间;在氮气环境下,随着WSx含量的增加复合膜的耐磨性能提高,其摩擦因数在0.03~0.10之间。
出处 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2015年第9期3002-3011,共10页 中国有色金属学报(英文版)
关键词 W/DLC/W-S-C composite film magnetron sputtering adhesion strength friction coefficient W/DLC/W-S-C复合膜 磁控溅射 结合强度 摩擦因数
  • 相关文献

参考文献28

  • 1SC’HARF T W, PRASAD S V, DUGGER M T, KOTULA P G. GOEKE R S, GRUBBS R K. Growth, structure, and tribological behavior of atomic layer-deposited tungsten disulphide solid lubricant coatings with applications to MEMS [J]. Acta Materialia,2006, 54:4731-4743.
  • 2王吉会,Hua Chen,E.Wieers,L.M.Stals,J.P.Celis.Comparison of tribological properties of industrial low friction coatings[J].中国有色金属学会会刊:英文版,2002,12(1):78-82. 被引量:2
  • 3WONG K C, LU X, COTTER J, EADIE D T, WONG P C, MITCHELL K A R. Surface and friction characterization of MoSi and WS2 third body thin films under simulated wheel/rail rolling-sliding contact [J]. Wear, 2008, 264: 526-534.
  • 4PRASAD S V, ZABINSKI J S, MCDEVITT N T. Friction behavior of pulsed laser deposited tungsten disulfide films [J]. Tribology Transactions, 1995, 38(1): 57-62.
  • 5WEISE G, MATTF.RN N, HERMANN H, TERESIAK A, BACHERI, BAUER H D, VINZEL-BERG H, REISS G, KREISSIG U, MADER M, MARKSCHLAGER P. Preparation, structure and properties of MoS.v films [J], Thin Solid Films, 1997, 298: 98*106.
  • 6XU Shu-sheng, GAO Xiao-ming, HU Ming, SUN Jia-yi, JIANG Dong, ZHOU Feng, LIU Wei-min, WENG Li-jun. Nanostructured WS2~Ni composite films for improved oxidation, resistance and tribological performance [J]. Applied Surface Science, 2014, 288: 15-25.
  • 7SCHARF T W, RAJENDRAN A, BANERJEE R, SEQUEDA F. Growth, structure and friction behavior of titanium doped tungsten disulphide (Ti-WSi) nanocomposite thin films [J]. Thin Solid Films, 2009,517: 5666-5675.
  • 8WANG Q, TU J P, ZHANG S C, LAI D M, PENG S M, GU B. Effect of Ag content on microstructure and tribological performance of WS2_Ag composite films [J], Surface and Coatings Technology,2006, 201: 1666-1670.
  • 9XIE Zhi-wen, WANG Lang-ping, WANG Xiao-feng, HUANG Lei, LU Yang, YAN Jiu-chun. Mechanical performance and corrosion behavior of TiAlSiN/WS2 multilayer deposited by multi-plasma immersion ion implantation and deposition and magnetron sputtering [J]. Transactions of Nonferrous Metals Society of China, 2011, 21 (S): s470-s475.
  • 10RENEVIER N M, FOX V C, TEER D G, HAMPSHIRE J. Coating characteristics and tribological properties of sputter-deposited M0S2 metal composite coatings deposited by closed field unbalanced magnetron sputter ion plating [J]. Surface and Coatings Technology,2000, 127:24-37.

二级参考文献18

  • 1Hirvonen J P, Koskinen J, Jervis J R, et al. Present progress in the development of low friction coatings [J]. Surf Coat Technol, 1996, 80: 139-150.
  • 2Cohen S R, Rapoport L, Ponomarev E A, et al. The tribological behavior of type Ⅱ textured MX2 (M=Mo, W; X=S, Se) films [J]. Thin Solid Films, 1998, 324: 190-197.
  • 3Wanstrand O, Larsson M, Hedenqvist P. Mechanical and tribological evaluation of PVD WC/C coatings [J]. Surf Coat Technol, 1999, 111: 247-254.
  • 4Roth D, Rau B, Roth S, et al. Large area and three-dimensional deposition of diamond-like carbon films for industrial application [J]. Surf Coat Technol, 1995, 74/75: 637-641.
  • 5Derflinger V, Brandle H, Zimmermann H. New hard/lubricant coating for dry machining [J]. Surf Coat Technol, 1999, 113: 286-292.
  • 6Fleischauer P D, Bauer R. Chemical and structural effects on the lubrication properties of sputtering MoS2 films [J]. Tribol Trans, 1988, 31(2): 239-250.
  • 7Spalvins T. A review of recent advances in solid film lubrication [J]. J Vac Sci Technol, 1987, A5(2): 212-219.
  • 8Donnet C. Advanced solid lubrication coatings for high vacuum environments [J]. Surf Coat Technol, 1996, 80: 151-156.
  • 9Hilton M R, Fleischauer P D. Applications of solid lubricant films in spacecraft [J]. Surf Coat Technol, 1992, 54-55: 435-441.
  • 10Fox V, Hampshire J, Teer D. MoS2/metal composite coatings deposited by closed-field unbalanced magnetron sputtering: tribological properties and industrial uses [J]. Surf Coat Technol, 1999, 112: 118-122.

共引文献1

同被引文献21

引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部