摘要
Titanylphthalocyanine （TiOPc） as hole transporting material （HTM） was successfully synthesized by a simple process with low cost. Perovskite solar cells using the TiOPc as HTM were fabricated and characterized. TiOPc as HTM plays an important role in increasing the power conversion efficiency （PCE） by minimizing recombi- nation losses at the perovskite/Au interface because TiOPc as HTM can extract photogenerated holes from the perovskite and then transport quickly these charges to the back metal electrode. In the research, the β-TiOPc gives a higher PCE than α-TiOPc for the devices due to sufficient transfer dynamics, The β-TiOPc was applied in perovskite solar cells without clopping to afford an impressive PCE of 5.05% under AM 1.5G illumination at the thickness of 40 nm which is competitive with spiro-OMeTAD at the same condition. The present work suggests a guideline for optimizing the photovoltaic properties ofperovskite solar cells using the TiOPc as the HTM.
Titanylphthalocyanine （TiOPc） as hole transporting material （HTM） was successfully synthesized by a simple process with low cost. Perovskite solar cells using the TiOPc as HTM were fabricated and characterized. TiOPc as HTM plays an important role in increasing the power conversion efficiency （PCE） by minimizing recombi- nation losses at the perovskite/Au interface because TiOPc as HTM can extract photogenerated holes from the perovskite and then transport quickly these charges to the back metal electrode. In the research, the β-TiOPc gives a higher PCE than α-TiOPc for the devices due to sufficient transfer dynamics, The β-TiOPc was applied in perovskite solar cells without clopping to afford an impressive PCE of 5.05% under AM 1.5G illumination at the thickness of 40 nm which is competitive with spiro-OMeTAD at the same condition. The present work suggests a guideline for optimizing the photovoltaic properties ofperovskite solar cells using the TiOPc as the HTM.
基金
supported by the National Nature Science Foundation of China (NO.21206110)
Tianjin Science and Technology Support Plan Key Projects (NO.13ZCZDGX00900)