Magnetic a-Fe2O3, γ-Fe2O3 and Fe3O4 were prepared by facile calcination under different temperature from K4[Fe（CN）6] as raw materials, in which the calcined products are a-Fe2O3, Fe3O4 and y-Fe203 at 400 or 700, 500, and 600 ℃, respectively. The as-prepared compounds were characterized by X-ray powder diffraction and scanning electron microscopy, and their magnetic behavior at room temperature was also studied. This method provided a simple approach to prepare different polymorphic forms of magnetic iron oxides, which may have potential applications in magnetic science, magnetic composite materials, magnetic core, magnetic separation and medical diagnostics.
Magnetic a-Fe2O3, γ-Fe2O3 and Fe3O4 were prepared by facile calcination under different temperature from K4[Fe（CN）6] as raw materials, in which the calcined products are a-Fe2O3, Fe3O4 and y-Fe203 at 400 or 700, 500, and 600 ℃, respectively. The as-prepared compounds were characterized by X-ray powder diffraction and scanning electron microscopy, and their magnetic behavior at room temperature was also studied. This method provided a simple approach to prepare different polymorphic forms of magnetic iron oxides, which may have potential applications in magnetic science, magnetic composite materials, magnetic core, magnetic separation and medical diagnostics.
基金
supported by the Funds of Fujian province department of education(No.JA14199)