河南某黄金冶炼渣铁品位为27.24%,铁主要以赤铁矿的形式存在。为回收该渣中铁,采用直接还原焙烧—弱磁选工艺进行试验。结果表明:在还原剂焦煤加入量为15%、氧化钙加入量为5%、焙烧温度为1 150℃、焙烧时间为80 min、焙烧产品磨细至-0.045 mm占75%、弱磁选磁场强度为60 k A/m时,可以获得铁品位为91.4%、回收率为79.5%的铁精矿,实现了该黄金冶炼渣中铁的高效回收。
There is 27. 24% iron in a gold smelting slag from Henan Province. The iron in the slag mainly exists in the form of hematite. Direct reduction roasting-low intensity magnetic separation process was conducted on the slag to recovery iron from this gold smelting slag. The results showed while the dosage of reducing agent is 15%,dosage of calcium oxide is 5%,roasting temperature is 1 150 ℃,roasting time is 80 min,and then ground the roasted product to-0. 045 mm accounted for75%,magnetic field intensity is 60 k A/m,the iron concentrate with iron grade of 91. 4% and iron recovery of 79. 5% can be obtained,high efficiently recovery of iron in slag was realized.
出处
《金属矿山》
CAS
北大核心
2015年第12期169-172,共4页
Metal Mine
基金
国家自然科学基金项目(编号:51404220)
国土资源部地质调查项目(编号:12120114021901)
河南省科技攻关项目(编号:152102310388)
关键词
黄金冶炼渣
直接还原焙烧
弱磁选
氧化钙
Gold smelting slag
Direct reduction roasting
Low intensity magnetic separation
Calcium oxide