To clarify the influence of Fe O and sulfur on solid state reaction between an Fe-Mn-Si alloy and Mn O-Si O2-Fe O oxides under the restricted oxygen diffusion flux, two diffusion couples with different sulfur contents in the oxides were produced and investigated after heat treatment at 1473 K. The experimental results were also compared with previous work in which the oxides contained higher Fe O. It was found that although the Fe O content in the oxides decreased from 3wt% to 1wt% which was lower than the content corresponding to the equilibrium with molten steel at 1873 K, excess oxygen still diffused from the oxides to solid steel during heat treatment at 1473 K and formed oxide particles. In addition, increasing the sulfur content in the oxides was observed to suppress the diffusion of oxygen between the alloy and the oxides.
To clarify the influence of Fe O and sulfur on solid state reaction between an Fe-Mn-Si alloy and Mn O-Si O2-Fe O oxides under the restricted oxygen diffusion flux, two diffusion couples with different sulfur contents in the oxides were produced and investigated after heat treatment at 1473 K. The experimental results were also compared with previous work in which the oxides contained higher Fe O. It was found that although the Fe O content in the oxides decreased from 3wt% to 1wt% which was lower than the content corresponding to the equilibrium with molten steel at 1873 K, excess oxygen still diffused from the oxides to solid steel during heat treatment at 1473 K and formed oxide particles. In addition, increasing the sulfur content in the oxides was observed to suppress the diffusion of oxygen between the alloy and the oxides.
基金
the National Natural Science Foundation of China (Nos. 51374021 and 51304016)
the Fundamental Research Funds for the Central Universities of China (No. FRF-TP-14-114A2)
Research Funds of State Key Laboratory of Advanced Metallurgy (No. 41603014)