摘要
To realize the comprehensive utilization of coal-fired industrial solid wastes, a novel high-strength board was prepared from calcium silicate slag, fly ash, and flue gas desulfurization(FGD) gypsum. The changes in mineral phases, chemical structure, and morphology during hydration were investigated by X-ray diffraction(XRD), Fourier transform infrared spectroscopy(FTIR), and scanning electron microscopy(SEM). A traditional board made from quartz and lime was prepared as a reference. The novel board not only consumes a lot of solid wastes, but also meets the strength requirement of the class-five calcium silicate board according to the Chinese Standard JC/T 564.2—2008. Microanalysis showed that hydrated calcium silicate gel(C-S-H(I)), ettringite, tobermorite, and xonotlite were successively generated in the novel board by synergistic hydration of the mixed solid wastes. The board strength was improved by the formation of tobermorite and xonotlite but decreased by unhydrated quartz. It was demonstrated that quartz was not completely hydrated in the traditional board. As a result, the flexural strength of the traditional board was much lower than that of the novel board.
To realize the comprehensive utilization of coal-fired industrial solid wastes, a novel high-strength board was prepared from calcium silicate slag, fly ash, and flue gas desulfurization(FGD) gypsum. The changes in mineral phases, chemical structure, and morphology during hydration were investigated by X-ray diffraction(XRD), Fourier transform infrared spectroscopy(FTIR), and scanning electron microscopy(SEM). A traditional board made from quartz and lime was prepared as a reference. The novel board not only consumes a lot of solid wastes, but also meets the strength requirement of the class-five calcium silicate board according to the Chinese Standard JC/T 564.2—2008. Microanalysis showed that hydrated calcium silicate gel(C-S-H(I)), ettringite, tobermorite, and xonotlite were successively generated in the novel board by synergistic hydration of the mixed solid wastes. The board strength was improved by the formation of tobermorite and xonotlite but decreased by unhydrated quartz. It was demonstrated that quartz was not completely hydrated in the traditional board. As a result, the flexural strength of the traditional board was much lower than that of the novel board.
基金
financial support of the National High-Tech Research and Development Program of China (No. 2012AA06A118)
the Natural Science Foundation of Inner Mongolia (No. 2014MS0521)
the Key Science & Technology Development Project of Baotou City (No. 2013Z1016)