咪唑啉类缓蚀剂对P110钢在CO_2注入井环空环境中应力腐蚀行为的影响 被引量:11

Effect of Imidazoline Corrosion Inhibitor on Stress Corrosion Cracking Behavior of P110 Steel in Simulated Annulus Environment in CO_2 Injection Wells
下载PDF
导出
摘要 目的研究咪唑啉类缓蚀剂对P110钢在CO2注入井环空环境中的应力腐蚀(SCC)行为的影响,为CO2注入井环空环境腐蚀防护方法的建立提供参考和依据。方法在实验室模拟的CO2驱注井环空环境中进行应力腐蚀试验、电化学测试和腐蚀形貌分析。根据现场提取的CO2注入井环空介质的成分分析结果配制模拟溶液,选用咪唑啉类缓蚀剂,调节模拟液p H至4。通入高纯N2进行除氧,以防止硫化物氧化。应力腐蚀试样采用三点弯试样,通过将试样的挠度控制为设定值来控制加载载荷。应力腐蚀试验和电化学试验均在密闭高压釜内进行。实验结束后,采用扫描电镜对腐蚀形貌进行观察。结果在CO2注入井环空环境下,咪唑啉缓蚀剂的浓度对P110钢的SCC行为有重要影响。在拉应力载荷存在时,添加足量的缓蚀剂对均匀腐蚀和SCC均具有较好的抑制效果,但当用量不足时,缓蚀剂的添加会增大P110钢的SCC敏感性,其SCC机制为氢脆与局部阳极溶解的混合机制。因此,P110钢在模拟CO2注入井的环空环境中会发生SCC,其机制为AD+HE机制。结论咪唑啉缓蚀剂的浓度对P110钢的SCC行为有重要影响,足量的缓蚀剂对均匀腐蚀和SCC均具有较好的抑制效果,但浓度不足时反而会增大SCC敏感性。 ABSTRACT:Objective To study the effect of imidazoline corrosion inhibitor on the stress corrosion cracking ( SCC) behavior of <br> P110 steel in simulated annulus environment in CO2 injection wells, in order to provide reference and basis for the establishment of protection method against corrosion in the annulus environment of CO2 injection wells. Methods P110 steel in simulated annulus environment in CO2 injection wells was treated by SCC tests, electrochemical measurements and corrosion morphology analysis. Ac-cording to the site-extracted component analysis results of annulus medium in the CO2 injection well, simulated solution was pre-pared in laboratory, imidazoline corrosion inhibitor was selected, and the pH of the simulated solution was adjusted to 4. Highly pure N2 was introduced to deoxidize, in order to prevent the oxidation of sulfide. Three-point bend specimen was used in the stress corrosion test, and the deflection of the sample was controlled at the set value to control the load. Both the stress corrosion test and electrochemical test were carried out in a closed autoclave. After the experiment, the corrosion morphology was observed by scan-ning electron microscope. Results In the annulus environment of the CO2 injection well, concentration of imidazoline corrosion in-hibitor had important effect on the SCC behavior of P110 steel. In the presence of tensile stress load, the addition of sufficient cor-rosion inhibitor had good inhibition effect on uniform corrosion and SCC, but when the dosage was insufficient, the addition of cor-rosion inhibitor would increase the SCC sensitivity of P110 steel, and the SCC mechanism was the mixed mechanism of local anodic dissolution and hydrogen embrittlement. Therefore,SCC occured on P110 steel in simulated annulus environment in CO2 injection wells, and its mechanism was AD+HE. Conclusion The concentration of imidazoline corrosion inhibitor posed a significant influ-ence on the SCC behavior of P110 steel. Adequate imidazoline corrosion inhibitor could well inhibit both uniform corrosion and SCC, while the addition of inadequate imidazoline corrosion inhibitor increased the SCC susceptibility instead.
出处 《表面技术》 EI CAS CSCD 北大核心 2015年第3期25-30,共6页 Surface Technology
基金 国家高技术研究发展计划(863计划 2012AA040105) 国家科技基础性工作专项(2012FY113000) 国家自然科学基金(51471034)~~
关键词 P110钢 应力腐蚀 环空环境 CO2注入 P110 Steel stress corrosion cracking annulus environment CO2injection
  • 相关文献

参考文献14

  • 1O. Yevtushenko,D. Bettge,S. Bohraus,R. B??ler,A. Pfennig,A. Kranzmann.Corrosion behavior of steels for CO 2 injection[J]. Process Safety and Environmental Protection . 2013
  • 2Ivana Jevremovi?,Marc Singer,Sr?an Ne?i?,Vesna Mi?kovi?-Stankovi?.Inhibition properties of self-assembled corrosion inhibitor talloil diethylenetriamine imidazoline for mild steel corrosion in chloride solution saturated with carbon dioxide[J]. Corrosion Science . 2013
  • 3J. Kittel,F. Ropital,F. Grosjean,E.M.M. Sutter,B. Tribollet.Corrosion mechanisms in aqueous solutions containing dissolved H 2 S. Part 1: Characterisation of H 2 S reduction on a 316L rotating disc electrode[J]. Corrosion Science . 2013
  • 4Tonglei Wang,Yongchen Song,Yuechao zhao,Yu Liu,Ningjun Zhu.Measurement of Immiscible CO 2 Flooding Processes and Permeability Reduction due to Asphaltene Precipitation by X-ray CT Imaging[J]. Energy Procedia . 2013
  • 5Corrosion of Metals and Alloys—Stress Corrosion Testing—Part 6:Preparation and Use of Precracked Specimens for Tests Under Constant Load or Constant Displacement. GB/T 15970.6—1998 .
  • 6Jing Guan,Li-Ping Xia,Li-Ying Wang,Jin-Feng Liu,Ji-Dong Gu,Bo-Zhong Mu.Diversity and distribution of sulfate-reducing bacteria in four petroleum reservoirs detected by using 16S rRNA and dsrAB genes[J]. International Biodeterioration & Biodegradation . 2013
  • 7ZIAEI S M R,KOKABI A H,NASR-ESFEHANI M.Sulfide Stress Corrosion Cracking and Hydrogen Induced Cracking of A216-WCC Wellhead Flow Control Valve Body. Case Studies in Engineering Failure Analysis . 2013
  • 8Dezhi Zeng,Rui Chen,Zhi Zhang,Liyun Shao,Guoping Li,Gang Tian,Taihe Shi.Research on Stress Corrosion Sensitivity of C110 Casing in Wellbore Protection Fluid[J]. Energy Procedia . 2012
  • 9Antony P. Joseph,Jürg Keller,Heriberto Bustamante,Philip L. Bond.Surface neutralization and H 2 S oxidation at early stages of sewer corrosion: Influence of temperature, relative humidity and H 2 S concentration[J]. Water Research . 2012 (13)
  • 10Z. Y. Liu,C. F. Dong,X. G. Li,Q. Zhi,Y. F. Cheng.Stress corrosion cracking of 2205 duplex stainless steel in H 2 S–CO 2 environment[J]. Journal of Materials Science . 2009 (16)

二级参考文献18

  • 1Shoesmith D W, Taylor P, Bailey M G, et al. Formation of Ferrous MonosulfJde Polymorphs During the Corrosion of Iron by Aqueous Hydrogen Sulfide at 21 "C [J]. Journal of the Electrochemical Society, 1980, 127(5): 1007.
  • 2Shoesmith D W, Rummery T E, Bailey M G, et al. Electro chemical Formation of Sulfur at Stainless Steel Surfaces [J]. Journal of the Electrochemical Society, 1980, 127(1): 27.
  • 3Kudo T, Tsuge H, Moroishi T. Stress Corrosion Cracking Re sistance of 22: Cr Duplex Stainless Steel in Simulated SourEnvironments [J] Corrosion, 1989, 45(10): 831.
  • 4Schmitt G. Effect of Elemental Sulfur on Corrosion in Sour Gas Systems [J] Corrosion, 1991, 47(4): 285.
  • 5AI-Hajji J N, Reda M R. Corrosion Behavior of Low Residual Carbon Steels in a Sour Environment [J]. Corrosion, 1993, 49 (5) : 363.
  • 6Ikeda A, Ueda M, Mukai S. CO2 Corrosion Behavior and Mechanism of Carbon Steel and Alloy Steel [C]//Remita E, Tribollet B, Sutter E, et al. Corrosion/1983. Houston.. Is.n.J, 1983.. 45.
  • 7Ma Houyi, Cheng Xiaoliang, Li Guiqiu, et al. The Influence of Hydrogen Sulfide on Corrosion of Iron Under Different Condi tions [J]. Corrosion Science, 2000, 42(10): 1669.
  • 8Ahelev E, Ramanarayanan T A, Bernasek S L. Iron Corrosion in COz/Brine at Low H2S Concentrations: An Electrochemical and Surface Science Study [J]. Journal of the Electrochemical Society, 2009, 156(9): C331.
  • 9Masamura K, Hashizume S, Sakai J, et al. Polarization Behav ior of High Alloy Octg in CO2 Environment as Affected by Chlorides and Sulfides [J]. Corrosion, 1987, 43(6): 359.
  • 10Pots B F M, Kapusta S D,'John R C. Improvements on De Waard Milliams Corrosion Prediction and Applications to Cor- rosion Management [C]//Scapin M, Sgorlon S, Tolomio M, et al. Corrosion/2002, Houston: Es.n.l, 2002: 235.

共引文献25

同被引文献207

引证文献11

二级引证文献103

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部