摘要
In this study, gecko-inspired polydimethylsiloxane （PDMS） microfiber surfaces were fabricated by combining Inductively Coupled Plasma （ICP） and micro-mold casting. The effect of roughness and surface energy of counterface on the adhesion of gecko-inspired microflber surfaces and its superhydrophobicity and wet self-cleaning were studied. The adhesion of gecko-inspired microfiber surfaces depended on the roughness of the eounterfaces due to the influences of contact area and interlocking mechanism. SEM images of interfaces between counterfaces with different roughness and gecko-inspired mi- crofiber surfaces revealed the matched and dis-matched contact directly. The gecko-inspired microfiber surface got the larger adhesive force from the higher surface energy counterface, which is consisted with Johnson-Kendall-Roberts （JKR） theory. The smaller dimension and lower duty ratio of microfibers on PDMS resulted in the increasing of Water Contact Angle （WCA） and the decreasing of Sliding Angle （SA） compared to those of smooth PDMS. Particularly, sample P-8-28-20 had the biggest WCA （155°） and SA （7°）, which displayed the superhydrophobicity and the best wet self-cleaning efficiency in all samples. The present studies showed that the roughness and surface energy of counterface both affected the adhesion of gecko-inspired microfiber surfaces. The smaller dimension and lower duty ratio of microfibers on PDMS endowed it with the superhydro- phobicity and the wet self-cleaning abilities.
In this study, gecko-inspired polydimethylsiloxane （PDMS） microfiber surfaces were fabricated by combining Inductively Coupled Plasma （ICP） and micro-mold casting. The effect of roughness and surface energy of counterface on the adhesion of gecko-inspired microflber surfaces and its superhydrophobicity and wet self-cleaning were studied. The adhesion of gecko-inspired microfiber surfaces depended on the roughness of the eounterfaces due to the influences of contact area and interlocking mechanism. SEM images of interfaces between counterfaces with different roughness and gecko-inspired mi- crofiber surfaces revealed the matched and dis-matched contact directly. The gecko-inspired microfiber surface got the larger adhesive force from the higher surface energy counterface, which is consisted with Johnson-Kendall-Roberts （JKR） theory. The smaller dimension and lower duty ratio of microfibers on PDMS resulted in the increasing of Water Contact Angle （WCA） and the decreasing of Sliding Angle （SA） compared to those of smooth PDMS. Particularly, sample P-8-28-20 had the biggest WCA （155°） and SA （7°）, which displayed the superhydrophobicity and the best wet self-cleaning efficiency in all samples. The present studies showed that the roughness and surface energy of counterface both affected the adhesion of gecko-inspired microfiber surfaces. The smaller dimension and lower duty ratio of microfibers on PDMS endowed it with the superhydro- phobicity and the wet self-cleaning abilities.