Nanoindentation test is performed on study the plastic and creep properties of the Sn-Ag-Cu （SAC） lead-free ball grid array （ BGA ） solder joints. The dynamic hardness of two kinds of solder joints decreases with indentation depth increase. SACO705 BiNi/ Cu exhibits a higher ultimate dynamic hardness and a smaller indentation depth than SAC305/ Cu. Then the strain hardening phenomenon of SAC305/ Cu is more obvious compared to that of SACO705 BiNi/ Cu. The indentation creep of SACO705BiNi/ Cu solder joint is lower than that of SAC305/ Cu solder joint before and after thermal shock. The creep rate sensitive index of SACBiNi/Cu solder joint is lower than that of solder joint. SACO705BiNi/Cu solder joint is superior to SAC305/Cu solder joint in the anti-creep property. The plasticity of SACOTOSBiNi/Cu and SAC305/Cu solder joints are similar. Compared with SAC305 solder, the SACO705 BiNi solder pe^forms higher hardness and solder creep resistance and still maintains a good plasticity.
Nanoindentation test is performed on study the plastic and creep properties of the Sn-Ag-Cu （SAC） lead-free ball grid array （ BGA ） solder joints. The dynamic hardness of two kinds of solder joints decreases with indentation depth increase. SACO705 BiNi/ Cu exhibits a higher ultimate dynamic hardness and a smaller indentation depth than SAC305/ Cu. Then the strain hardening phenomenon of SAC305/ Cu is more obvious compared to that of SACO705 BiNi/ Cu. The indentation creep of SACO705BiNi/ Cu solder joint is lower than that of SAC305/ Cu solder joint before and after thermal shock. The creep rate sensitive index of SACBiNi/Cu solder joint is lower than that of solder joint. SACO705BiNi/Cu solder joint is superior to SAC305/Cu solder joint in the anti-creep property. The plasticity of SACOTOSBiNi/Cu and SAC305/Cu solder joints are similar. Compared with SAC305 solder, the SACO705 BiNi solder pe^forms higher hardness and solder creep resistance and still maintains a good plasticity.
基金
This work was supported by National Natural Science Foundation of China （ Grant No. 51174069 and 51075107） and Research Special Funds for Technology Creative Talents of Harbin （Grant No. 2013RFQXJ166）.