By applying ultrasonic-MIG welding as research object, the behaviors of welding arc were analyzed with varied ultrasonic parameters in welding using arc images recorded by high-speed camera. The influences of the current by exciting ultrasonic and the height and shape of ultrasonic radiator on welding arc were studied. Results showed that when the current was 150 mA, ultrasonic showed most distinct compressive effect on arc. The compressive volumes of arc length at different heights were calculated by adjusting the height of ultrasonic radiator continuously from 10 mm to 35 mm, there were three maximum points. The compressive degrees of them reduced successively. By utilizing different shapes of ultrasonic radiator, it revealed that ultrasonic radiator with spherical crown surface showed better compressive effect in a larger welding standard scope. When radius of radiator increased, axial compressive volume of arc enlarged, while an increasing curvature radius led to mare distinct radial compression of arc.
By applying ultrasonic-MIG welding as research object, the behaviors of welding arc were analyzed with varied ultrasonic parameters in welding using arc images recorded by high-speed camera. The influences of the current by exciting ultrasonic and the height and shape of ultrasonic radiator on welding arc were studied. Results showed that when the current was 150 mA, ultrasonic showed most distinct compressive effect on arc. The compressive volumes of arc length at different heights were calculated by adjusting the height of ultrasonic radiator continuously from 10 mm to 35 mm, there were three maximum points. The compressive degrees of them reduced successively. By utilizing different shapes of ultrasonic radiator, it revealed that ultrasonic radiator with spherical crown surface showed better compressive effect in a larger welding standard scope. When radius of radiator increased, axial compressive volume of arc enlarged, while an increasing curvature radius led to mare distinct radial compression of arc.
基金
This study was supported by National Natural Science Foundation of China （Grant No. 51275134） and the Key Program of the National Natural Science Foundation of China （Grant No. 51435004）.