Effects of Nano-Y_2O_3 and Sintering Parameters on the Fabrication of PM Duplex and Ferritic Stainless Steels

Effects of Nano-Y_2O_3 and Sintering Parameters on the Fabrication of PM Duplex and Ferritic Stainless Steels
原文传递
导出
摘要 Here we report the effects of nano-Y203 addition, sintering atmosphere and time during on the fabrication of PM duplex and ferritic stainless steels composites by dual-drive planetary milling of elemental Fe, Cr and Ni powders followed by conventional pressureless sintering. Yttria-free and yttria-dispersed duplex and ferritic stainless steels are fabricated by conventional sintering at 1000, 1200 and 1400 ℃ temperatures under argon atmosphere. In another set of experiment, yttria-free and yttria-dispersed duplex and ferritic stainless steels are consolidated at 1000 ℃ for l h under nitrogen atmosphere to study the effect of sintering atmosphere. It has been found that densities of duplex and yttria- dispersed duplex stainless steel increase from 71% to 91% and 78% to 94%, respectively, with the increase in sintering temperature. Similarly, hardness value increases from 257 to 567 HV25 in case of duplex, and from 332 to 576 HV25 in yttria-dispersed duplex stainless steel. X-ray diffraction analysis shows the domination of more intense austenite phase than ferrite at higher sintering temperature and also in nitrogen atmosphere. It is also evident that addition of yttria enhances phase transformation from a-Fe to 7-Fe. Duplex and yttria-dispersed duplex stainless steels exhibit the maximum com- pressive yield strength of 360 and 312 MPa, respectively. Here we report the effects of nano-Y203 addition, sintering atmosphere and time during on the fabrication of PM duplex and ferritic stainless steels composites by dual-drive planetary milling of elemental Fe, Cr and Ni powders followed by conventional pressureless sintering. Yttria-free and yttria-dispersed duplex and ferritic stainless steels are fabricated by conventional sintering at 1000, 1200 and 1400 ℃ temperatures under argon atmosphere. In another set of experiment, yttria-free and yttria-dispersed duplex and ferritic stainless steels are consolidated at 1000 ℃ for l h under nitrogen atmosphere to study the effect of sintering atmosphere. It has been found that densities of duplex and yttria- dispersed duplex stainless steel increase from 71% to 91% and 78% to 94%, respectively, with the increase in sintering temperature. Similarly, hardness value increases from 257 to 567 HV25 in case of duplex, and from 332 to 576 HV25 in yttria-dispersed duplex stainless steel. X-ray diffraction analysis shows the domination of more intense austenite phase than ferrite at higher sintering temperature and also in nitrogen atmosphere. It is also evident that addition of yttria enhances phase transformation from a-Fe to 7-Fe. Duplex and yttria-dispersed duplex stainless steels exhibit the maximum com- pressive yield strength of 360 and 312 MPa, respectively.
出处 《Acta Metallurgica Sinica(English Letters)》 SCIE EI CAS CSCD 2016年第1期58-71,共14页 金属学报(英文版)
基金 Financial support for this work from the Council of Scientific & Industrial Research(CSIR),India(Grant No. 22/561/11/EMR Ⅱ Dated 11.04.2011)
关键词 Nano-Y2O3 Composites Stainless steel Powder metallurgy (PM) Mechanical properties Microstructure Phase transitions Nano-Y2O3 Composites Stainless steel Powder metallurgy (PM) Mechanical properties Microstructure Phase transitions
  • 相关文献

参考文献52

  • 1R. Shashanka, D. Chaira, B.E. Kumara Swamy, Int. J. Sci. Eng. Res. 6, 1863 (2015).
  • 2C. Petterson, S. Fager, Welding practice for the sandvik duplex stainless steels SAF2304, SAF2205 and SAF2507, vol. $811 (AB Sandvik Steel, Sweden, 1995), p. 1.
  • 3W.F. Smith, Structure and Properties of Engineering Alloys, 2nd edn. (The University of Michigan, McGraw Hill, 1981).
  • 4Y.Q. Wang, B. Yang, J. Han, F. Dong, Y.L. Wang, Pro. Eng. 36, 88 (2012).
  • 5R. Shashanka, D. Chaira, B.E. Kumara Swamy, Int. J. Elec- trochem. Sci. 10, 5586 (2015).
  • 6H. Miyamoto, T. Mirnaki, S. Hashimoto, Mater. Sci. Eng. A 319, 779 (2001).
  • 7T. Liang, X. Hu, X. Kang, D. Li, Acta Metall. Sin. (Engl. Lett.) 26, 517 (2013).
  • 8L.A. Dobrzanski, Z. Brytan, M. Actis Grande, M. Rosso, Arch. Mater. Sci. Eng. 28, 217 (2007).
  • 9X. Li, J. Shu, L. Chen, H. Bi, Acta Metall. Sin. (Engl. Lett.) 27, 501 (2014).
  • 10C. Suryanarayana, Prog. Mater. Sci. 46, 1 (2001).

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部