通过阴极保护电位测量、污损生物检测、水下船板超声测厚及牺牲阳极工作状态检查等几方面的检测,评价了长期系泊于青岛中港的海鸥浮码头海水全浸区钢铁的腐蚀失效情况,并根据上述几方面的检测结果,对其腐蚀失效的原因进行了综合分析。
Steel corrosion failure condition at Qingdao Zhonggang Floating Wharf was evaluated through cathodic protection potential measurement, fouling organism, the underwater ship ultrasonic thickness measurement and sacrificial anode working status. The failure reasons were analyzed based on the tests results.