Si对铸造Mg97ZnY2合金组织及性能的影响 被引量:2

Effects of Si on Microstructure and Mechanical Properties of Mg97ZnY2 Alloy
下载PDF
导出
摘要 采用普通铸造法制备了Si增强的Mg97ZnY2合金,研究了不同Si含量对Mg97Zn1Y2合金组织及力学性能的影响,利用光学显微镜(OM)观察金相组织,XRD分析了加入微量Si的Mg97ZnY2合金组织及相组成,测试了合金硬度和室温拉伸力学性能。结果表明:加入一定量Si后,Mg97Zn1Y2合金组织中形成颗粒状Mg_2Si相及亚稳定Mg_5Si_6相,在凝固过程中富集于固-液界面前沿,阻碍α-Mg树枝晶的自由长大,从而细化合金铸态组织;随着Si的含量增加,合金的硬度不断提高,当含量为1.8%时,合金的硬度达到95.5 HV,提高了18.5%;加入0.2wt%Si的Mg97ZnY2合金抗拉强度和伸长率均高于铸态Mg97ZnY2合金,抗拉强度达到220 MPa,伸长率为10%,其抗拉强度增加了24%,伸长率增加了37%。 Mg97ZnY2 alloys enhanced by Si were prepared using common casting method. The effects of Si contents on microstructure and mechanical properties of Mg97ZnY2 alloy were investigated. The microstructures were observed by the optical microscope (OM) and the phase components of the Mg97ZnY2 alloy with or without Si were analyzed by X-Ray diffraction (XRD). Meanwhile, the tensile properties and hardness at room temperature were tested. The results show that the metastable Mg^Si6 phase and the Mg2Si phase particles were emerged among the solid-liquid interface of the Mg97ZnY2 alloy during solidification process, this refining the casting alloy. The hardness of alloy was improved with the increasing of the content of element Si. The hardness of alloy is 95.5 HV when the content of element Si reaches 1.8%, which is increased by 18.5%. The tensile strength and elongation of Mg97ZnY2 alloy after adding 0.2wt%Si are higher than that of casting Mg97ZnY2 alloy, tensile strength reaches 220 MPa and the elongation is 10%. The tensile strength and elongation is increased by 24% and 37%, respectively.
出处 《铸造技术》 CAS 北大核心 2016年第2期201-204,共4页 Foundry Technology
基金 国家自然科学基金资助项目(51361010)
关键词 镁合金 Si变质 力学性能 magnesium alloy Si modification mechanical properties
  • 引文网络
  • 相关文献

参考文献9

  • 1Kawamura Y,Hayashi K,Inoue A,et al.Rapidly solidification/powder metallurgy Mg97Zn1Y2 alloys with excellent tensile yield strength above 600MPa[J].Materials Transactions,2001,42(7):1172-1176.
  • 2Zhang J,Fan Z,Wang Y Q,et al.Microstructural development of Al15wt.%Mg2Si in situ composite with mischmetal addition[J].Materials Science and Engineering A,2000,281:104-112.
  • 3Andersen S J,Zandbergen H W,Jansen J,et al.Crystal structure of theβ'phase in Al-Mg-Si alloys[J].Acta mater,1998,9(46):3283-3298.
  • 4Yasuya Ohmori,Long Chau Doan,Yoshitsugu Mastuura,et al.Morphology and crystallography ofβ-Mg2Si precipitation in Al-Mg-Si alloys[J].Material Transactions,2001,12(42):2576-2583.
  • 5Katsuyoshi KONDOH,Takashi YAMAGUCH,Tadashi SERIAWA.Surface modification of magnesium alloy by Mg2Si coating technology[J].JSME International Journal,2005,4(48):264-268.
  • 6Huisa M A,Chen J H,Zandbergen H W,et al.Sluiter phase stability and structural relations of nanometer-sized,matrix-embedded precipitate phases in Al-Mg-Si alloys in the late stages of evolution[J].Acta Materialia,2006,54:2945-2955.
  • 7Zhang H,Wang Y,Shang S L,et al.Solvus boundaries of(meta)stable phases in the Al-Mg-Si system:First-principles phonon calculations and thermodynamic modeling[J].Computer Coupling of Phase Diagrams and Thermo chemistry,2010(34):20-25.
  • 8安健,徐阳.Si掺杂Mg96Zn1Y3合金的组织性能及变形为研究[D].吉林:吉林大学,2007.
  • 9黄正华,郭学锋,张忠明,徐春杰.Si对AZ91D镁合金显微组织与力学性能的影响[J].材料工程,2004,32(6):28-32. 被引量:42

二级参考文献3

共引文献41

同被引文献11

引证文献2

二级引证文献8

;
使用帮助 返回顶部