The effect of synthesis methods on the activity of V/Ce/WTi catalysts was investigated for the selective catalytic reduction（SCR） of NO_x by NH_3. V/Ce/WTi-DP（deposition precipitation） catalyst showed excellent NH_3-SCR performance, especially the better medium-temperature activity and the less N_2O formation than V/Ce/WTi-IMP（impregnation）. These catalysts were characterized by X-ray diffraction（XRD）, Brumauer-Emmett-Teller（BET）, X-ray photoelectron spectroscopy（XPS）, temperature-programmed reduction（H_2-TPR）, and in situ DRIFTS techniques. The XPS and H_2-TPR results revealed that V/Ce/WTi-DP exhibited more surface Ce species, higher level of Oα and higher reducibility of Ce species. Reflected by in situ DRIFTS results, the deposition precipitation method（DP） contributed to a greater amount of weakly adsorbed NO_2, monodentate nitrate and NH_3 species with better reactive activity. Meanwhile, the cis-N_2O_2^（2-） species, an intermediate for N_2O formation, was very limited. As a result, these advantages brought about the superior SCR activity and N_2 selectivity for V/Ce/WTi-DP.
The effect of synthesis methods on the activity of V/Ce/WTi catalysts was investigated for the selective catalytic reduction（SCR） of NO_x by NH_3. V/Ce/WTi-DP（deposition precipitation） catalyst showed excellent NH_3-SCR performance, especially the better medium-temperature activity and the less N_2O formation than V/Ce/WTi-IMP（impregnation）. These catalysts were characterized by X-ray diffraction（XRD）, Brumauer-Emmett-Teller（BET）, X-ray photoelectron spectroscopy（XPS）, temperature-programmed reduction（H_2-TPR）, and in situ DRIFTS techniques. The XPS and H_2-TPR results revealed that V/Ce/WTi-DP exhibited more surface Ce species, higher level of Oα and higher reducibility of Ce species. Reflected by in situ DRIFTS results, the deposition precipitation method（DP） contributed to a greater amount of weakly adsorbed NO_2, monodentate nitrate and NH_3 species with better reactive activity. Meanwhile, the cis-N_2O_2^（2-） species, an intermediate for N_2O formation, was very limited. As a result, these advantages brought about the superior SCR activity and N_2 selectivity for V/Ce/WTi-DP.
基金
supported by the Grant from the China Huadian Science and Technology Institute(CHDI.KJ-20)
the National High-Tech Research and Development Program of China(863,2011AA03A405)